环氧大豆油和硅氧烷改性水性聚氨酯胶黏剂

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 环氧大豆油和硅氧烷改性水性聚氨酯胶黏剂
- Waterborne polyurethane adhesive modified by epoxy oil soybean and 3-aminopropyltriethoxysilane
- 化工学报 2014年第11期页码：4599-4606
- 作者机构：
  
  华南理工大学化学与化工学院,广东,广州,510640
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.11.055
  中图分类号： Q323.8
- 网络首发：2014-11-05，
  
  纸质出版：2014-11-05
- 稿件说明：
移动端阅览
何飞强, 傅和青, 周威. 环氧大豆油和硅氧烷改性水性聚氨酯胶黏剂[J]. 化工学报, 2014,(11):4599-4606.

HE Feiqiang, FU Heqing, ZHOU Wei. Waterborne polyurethane adhesive modified by epoxy oil soybean and 3-aminopropyltriethoxysilane[J]. CIESC Journal, 2014, (11): 4599-4606.
何飞强, 傅和青, 周威. 环氧大豆油和硅氧烷改性水性聚氨酯胶黏剂[J]. 化工学报, 2014,(11):4599-4606. DOI： 10.3969/j.issn.0438-1157.2014.11.055.

HE Feiqiang, FU Heqing, ZHOU Wei. Waterborne polyurethane adhesive modified by epoxy oil soybean and 3-aminopropyltriethoxysilane[J]. CIESC Journal, 2014, (11): 4599-4606. DOI： 10.3969/j.issn.0438-1157.2014.11.055.

摘要

以环氧大豆油(ESO)与3-氨基丙基三乙氧基硅烷(KH550)双重交联改性水性聚氨酯(WPU).通过FTIR、TG、DSC、DMA、AFM、粒径分析仪、拉力试验机等仪器对改性的水性聚氨酯进行了表征.研究了ESO和KH550的含量对水性聚氨酯乳液、胶膜以及胶黏剂性能的影响.分析了KH550对水性聚氨酯结晶性能和微相分离的影响.研究发现

随着ESO与KH550的加入

水性聚氨酯乳液的性能得到改善

胶膜的吸水率先减小后增大

拉伸强度逐渐增大

断裂伸张率逐渐减小.水性聚氨酯胶黏剂对PVC的T-剥离强度先增大后减小.随着KH550含量的增加

热稳定性逐步改善

结晶性降低

软段与硬段相混合程度提高.当ESO为4%、KH550为2%(均为质量分数)时

水性聚氨酯胶黏剂的综合性能最好.

Abstract

Waterborne polyurethane (WPU) modified by epoxy soybean oil (ESO) and 3-aminopropyltriethoxysilane (KH550) were synthesized. The properties of the modified WPU were characterized by FTIR

DSC

DMA

AFM

particle size analyzer and tensile test machine. The effects of contents of ESO and KH550 on the properties of WPU emulsion

its film and adhesive strength were studied. And the effect of KH550 on the crystallinity and microphase separation of WPU was analyzed. With the increase of contents of ESO and KH550

the properties of WPU dispersion were improved

the water absorption of WPU film decreased first

and then increased. Tensile strength increased

while elongation at break decreased. The T-peel strength of the adhesive to PVC/PVC increased first

and then decreased. With increasing KH550 content

thermal stability of the WPU film was improved

crystallinity decreased

degree of mixing of soft segment phase and hard segment phase was enhanced. When the contents of ESO and KH550 were 4% and 2%(mass)

respectively

the properties of WPU adhesive were perfect.

关键词

Keywords

references

浏览量

508

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

HDI/IPDI对水性聚氨酯及胶膜性能的影响

羟基-炔点击化学改性半乳甘露聚糖薄膜的制备及性能研究

液晶弹性体温度自适应润湿性表面沸腾特性研究

氢-摩擦耦合作用下橡胶O形密封圈的损伤行为数值研究

锂离子电池水性黏结剂的改性策略及应用研究进展