- NaOH改性MnO₂/γ-Al₂O₃催化尿素醇解合成碳酸丙烯酯
- Synthesis of propylene carbonate from urea and 1,2-propylene glycol over MnO₂/γ-Al₂O₃ catalyst modified by NaOH
- 化工学报 2014年第11期页码：4333-4339
- 作者机构：
  
  武汉工程大学绿色化工过程教育部重点实验室, 湖北省新型反应器与绿色化学工艺重点实验室,湖北,武汉,430074
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.11.017
  中图分类号： 63
- 网络首发：2014-11-05，
  
  纸质出版：2014-11-05
- 稿件说明：
移动端阅览
杜治平, 林志坤, 陈方胜, 等. NaOH改性MnO₂/γ-Al₂O₃催化尿素醇解合成碳酸丙烯酯[J]. 化工学报, 2014,(11):4333-4339. DOI: 10.3969/j.issn.0438-1157.2014.11.017.

DU Zhiping, LIN Zhikun, CHEN Fangsheng, et al. Synthesis of propylene carbonate from urea and 1,2-propylene glycol over MnO₂/γ-Al₂O₃ catalyst modified by NaOH[J]. CIESC Journal, 2014, (11): 4333-4339. DOI: 10.3969/j.issn.0438-1157.2014.11.017.
杜治平, 林志坤, 陈方胜, 等. NaOH改性MnO₂/γ-Al₂O₃催化尿素醇解合成碳酸丙烯酯[J]. 化工学报, 2014,(11):4333-4339. DOI: 10.3969/j.issn.0438-1157.2014.11.017. DOI：

DU Zhiping, LIN Zhikun, CHEN Fangsheng, et al. Synthesis of propylene carbonate from urea and 1,2-propylene glycol over MnO₂/γ-Al₂O₃ catalyst modified by NaOH[J]. CIESC Journal, 2014, (11): 4333-4339. DOI: 10.3969/j.issn.0438-1157.2014.11.017. DOI：

摘要

采用超声浸渍法制备了MnO2/γ-Al2O3催化剂

并用碱和盐对其进行了改性.采用X射线衍射仪(XRD)、CO2-TPD对改性后的MnO2/γ-Al2O3催化剂进行了表征

研究了改性后催化剂在尿素醇解合成碳酸丙烯酯(PC)反应中的催化性能.研究结果表明

NaOH改性MnO2/γ-Al2O3催化剂具有最好的催化性能;同时催化剂的焙烧时间、焙烧温度以及NaOH改性量影响催化剂表面碱性活性中心的数量和强度

其中中强碱的增加是改性后催化剂活性提高的主要原因.在NaOH用量为MnO2质量的10%

400℃焙烧2h后

改性MnO2/γ-Al2O3催化剂表面的中强碱量最大

催化活性最高

PC收率与选择性分别达86.9%、91.8%.

Abstract

MnO2/γ-Al2O3 catalyst was prepared by ultrasonic impregnation and modified by alkali or salt. The modified MnO2/γ-Al2O3 was characterized by X-ray diffraction (XRD)

temperature-programmed desorption of CO2(CO2-TPD). Catalytic performances were investigated in urea alcoholysis to propylene carbonate (PC). The activity of MnO2/γ-Al2O3 catalyst modified by NaOH was the best. At the same time

calcination temperature

calcination time and amount of NaOH affected the quantity and intensity of basic activity centers on the surface of the modified catalyst. The increase of moderately basic activity center was the main reason for the catalyst activity improvement after modification. When the MnO2/γ-Al2O3 catalyst was modified by 10% NaOH

and calcined at 400℃ for 2 h

the quantity of moderately basic activity center on the surface was the most

which led to the highest activity. Yield and selectivity of PC were up to 86.9% and 91.8%

respectively.

关键词

Keywords

references

浏览量

253

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

尿素均匀沉淀法合成CeO2-Al2O3载体负载Pt催化剂的CO氧化性能

催化剂形貌对沸腾床渣油加氢Ni-Mo/Al2O3 催化剂活性位的影响机制

全钒液流电池石墨毡电极的Ga2O3修饰

过渡金属基氮掺杂炭的构筑及其脱硫性能研究

原位水热法可控合成Bi2MoO6/MoO3复合纤维及其高效光催化产氢性能