聚乳酸/环氧大豆油共混物的性能

赵永青; 陈福泉; 冯彦洪; 瞿金平

doi:10.3969/j.issn.0438-1157.2014.10.059

您当前的位置：

首页 >

文章列表页 >

聚乳酸/环氧大豆油共混物的性能

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 聚乳酸/环氧大豆油共混物的性能
- Properties of poly(lactic acid)/epoxidized soybean oil blends
- 化工学报 2014年第10期页码：4197-4202
- 作者机构：
  
  1. 华南理工大学聚合物成型加工工程教育部重点实验室,广东,广州,510640
  2. 华南理工大学制浆造纸工程国家重点实验室,广东,广州,510640
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.10.059
  中图分类号： Q320.66
- 网络首发：2014-10-05，
  
  纸质出版：2014-10-05
- 稿件说明：
移动端阅览
赵永青, 陈福泉, 冯彦洪, 等. 聚乳酸/环氧大豆油共混物的性能[J]. 化工学报, 2014,(10):4197-4202.

ZHAO Yongqing, CHEN Fuquan, FENG Yanhong, et al. Properties of poly(lactic acid)/epoxidized soybean oil blends[J]. CIESC Journal, 2014, (10): 4197-4202.
赵永青, 陈福泉, 冯彦洪, 等. 聚乳酸/环氧大豆油共混物的性能[J]. 化工学报, 2014,(10):4197-4202. DOI： 10.3969/j.issn.0438-1157.2014.10.059.

ZHAO Yongqing, CHEN Fuquan, FENG Yanhong, et al. Properties of poly(lactic acid)/epoxidized soybean oil blends[J]. CIESC Journal, 2014, (10): 4197-4202. DOI： 10.3969/j.issn.0438-1157.2014.10.059.

摘要

聚乳酸（PLA）与环氧大豆油（ESO）经熔融共混制得具有高韧性的PLA/ESO共混物，并研究了ESO含量对PLA微观形态、力学和流变性能的影响规律。结果表明：ESO可显著降低PLA的熔体黏度，提高PLA的韧性；PLA/ESO共混物在低ESO含量（10%）时为部分相容，而在高ESO含量（20%和30%）时发生了相分离，从而使共混物的断裂伸长率和冲击强度随ESO含量增加先增大后减小，且分别在ESO含量为20%和15%时达到最大值，约为PLA的17倍和2.9倍，而拉伸强度则随之减小。

Abstract

Poly(lactic acid) (PLA) and epoxidized soybean oil (ESO) was melt blended to prepare the PLA/ESO blends with high toughness. The effects of ESO contents on the phase morphologies

mechanical and rheological properties of the prepared PLA/ESO blends were investigated. The introduction of ESO significantly decreased melt viscosity and improved toughness of PLA. The PLA/ESO blend with low ESO content (10%) was a partially miscible system

whereas that with high ESO content (20% and 30%) exhibited distinct phase separation. Elongation at break and impact strength of the blends increased firstly and then decreased with increasing ESO content. The former reached the maximum value (17 times that of PLA) at ESO content of 20%

and the latter reached the maximum value (2.9 times that of PLA) at ESO content of 15%. Tensile strength of the blends decreased with increasing ESO content.

关键词

Keywords

references

浏览量

323

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

阻燃型全生物基多元醇聚氨酯泡沫的制备及性能研究

双面组合槽型干气密封性能分析与结构优化

用于软包装生物基聚氨酯胶黏剂的制备及耐水热性能研究

基于2，5-呋喃二甲酸的三元无规共聚酯PBSF的制备与性能

新型柔性坝箔片端面气膜密封变形协调分析及性能智能优化