- 钙铝比对11.3CaO·7Al₂O₃微观结构及其溶出性能的影响
- Influence of calcium/aluminum ratio on microstructure and leaching of 11.3CaO·7Al₂O₃
- 化工学报 2014年第10期页码：4183-4190
- 作者机构：
  
  河北科技大学材料科学与工程学院, 河北省材料近净成形技术重点实验室,河北,石家庄,050018
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.10.057
  中图分类号： F803.2+1
- 网络首发：2014-10-05，
  
  纸质出版：2014-10-05
- 稿件说明：
移动端阅览
王波, 宗书凤, 孙会兰, 等. 钙铝比对11.3CaO·7Al₂O₃微观结构及其溶出性能的影响[J]. 化工学报, 2014,(10):4183-4190. DOI: 10.3969/j.issn.0438-1157.2014.10.057.

WANG Bo, ZONG Shufeng, SUN Huilan, et al. Influence of calcium/aluminum ratio on microstructure and leaching of 11.3CaO·7Al₂O₃[J]. CIESC Journal, 2014, (10): 4183-4190. DOI: 10.3969/j.issn.0438-1157.2014.10.057.
王波, 宗书凤, 孙会兰, 等. 钙铝比对11.3CaO·7Al₂O₃微观结构及其溶出性能的影响[J]. 化工学报, 2014,(10):4183-4190. DOI: 10.3969/j.issn.0438-1157.2014.10.057. DOI：

WANG Bo, ZONG Shufeng, SUN Huilan, et al. Influence of calcium/aluminum ratio on microstructure and leaching of 11.3CaO·7Al₂O₃[J]. CIESC Journal, 2014, (10): 4183-4190. DOI: 10.3969/j.issn.0438-1157.2014.10.057. DOI：

摘要

通过高温烧结法在不同钙铝比（C/A）的条件下合成了铝酸钙熟料。利用XRD对不同C/A下合成产物进行物相分析，对含量进行半定量分析，并计算其晶格常数。采用SEM观察不同C/A下合成产物的显微结构，并通过EDS佐证所得物相；最后研究了不同C/A下氧化铝的溶出性能。结果表明：当C/A<1.6时得到的产物为CaO·Al2O3和11.3CaO·7Al2O3（C11.3A7），且随着C/A的增大，C11.3A7的含量增高，氧化铝的溶出率提高；当C/A＝1.6时得到的产物只有C11.3A7，溶出率达到最大；当C/A>1.6时由于3CaO·Al2O3的形成，溶出率有所降低。C11.3A7晶格中CaO的缺失，促进了溶出反应的进行。

Abstract

Calcium aluminate clinkers with different calcium/aluminum ratios (C/A) were obtained by the high-temperature sintering method. Phase composition

phase semi-quantitative content and crystal constant of sinter were studied with different C/A by XRD. SEM and EDS were used to observe microstructure and element contents. The alumina leaching property of sinter was studied. When C/A was lower than 1.6

the products were CaO·Al2O3 and 11.3CaO·7Al2O3 (C11.3A7) and increase of calcium/aluminum ratio could lead to increase in the content of C11.3A7 and leaching ratio of alumina. When C/A was 1.6

the phase was almost completely C11.3A7 and the leaching rate of alumina reached a maximum. When C/A was higher than 1.6

the products were C11.3A7 and 3CaO·Al2O3

and the leaching rate of alumina decreased accordingly. The lack of CaO in C11.3A7 lattice improved the leaching reaction.

关键词

Keywords

references

浏览量

536

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

煤气化熔渣结构的多尺度研究进展

尿素均匀沉淀法合成CeO2-Al2O3载体负载Pt催化剂的CO氧化性能

Ca种类对准东煤灰烧结特性影响

氯化法钛白氧化反应器内颗粒碰撞行为及生成演化过程理论分析

振动往复螺旋强化传热性能及结晶垢微观形貌分析研究

钙铝比对11.3CaO·7Al2O3微观结构及其溶出性能的影响

Influence of calcium/aluminum ratio on microstructure and leaching of 11.3CaO·7Al2O3

DOI：10.3969/j.issn.0438-1157.2014.10.057

摘要

Abstract

关键词

Keywords

references

钙铝比对11.3CaO·7Al₂O₃微观结构及其溶出性能的影响

Influence of calcium/aluminum ratio on microstructure and leaching of 11.3CaO·7Al₂O₃