表面硅烷预处理/环氧镁铝复合涂层体系对铝合金的保护性能

表面与界面工程 | 更新时间：2025-12-10

- 表面硅烷预处理/环氧镁铝复合涂层体系对铝合金的保护性能
- Protection performance of silane pretreatment/Mγ-Al rich epoxy coating for aluminum alloy
- 化工学报 2014年第10期页码：4049-4055
- 作者机构：
  
  北京化工大学材料科学与工程学院, 材料电化学过程与技术北京市重点实验室,北京,100029
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.10.039
  中图分类号： G174.4
- 网络首发：2014-10-05，
  
  纸质出版：2014-10-05
- 稿件说明：
移动端阅览
张倩, 左禹, 唐聿明. 表面硅烷预处理/环氧镁铝复合涂层体系对铝合金的保护性能[J]. 化工学报, 2014,(10):4049-4055.

ZHANG Qian, ZUO Yu, TANG Yuming. Protection performance of silane pretreatment/Mγ-Al rich epoxy coating for aluminum alloy[J]. CIESC Journal, 2014, (10): 4049-4055.
张倩, 左禹, 唐聿明. 表面硅烷预处理/环氧镁铝复合涂层体系对铝合金的保护性能[J]. 化工学报, 2014,(10):4049-4055. DOI： 10.3969/j.issn.0438-1157.2014.10.039.

ZHANG Qian, ZUO Yu, TANG Yuming. Protection performance of silane pretreatment/Mγ-Al rich epoxy coating for aluminum alloy[J]. CIESC Journal, 2014, (10): 4049-4055. DOI： 10.3969/j.issn.0438-1157.2014.10.039.

摘要

在LY12铝合金表面制备了一层硅烷膜，研究了硅烷膜对铝合金表面富镁铝环氧涂层性能的影响。硅烷处理后，形成了硅烷膜与基体之间Si-O-Al共价键以及硅烷膜内部的Si-O-Si 结构，而硅烷膜中未成键的硅醇基团-OH以及R-的环氧基团与涂层中的有机组分反应成键或通过范德华力发生交联互穿，使铝合金基体与环氧镁铝复合涂层之间形成更加牢固的交联互穿网络结构（IPN），镁铝复合涂层在LY12铝合金基体上的附着力明显提高。马丘测试和电化学阻抗测试结果表明，硅烷处理改善了LY12铝合金表面镁铝复合涂层的整体屏蔽性能，使涂层体系的保护效果显著提高，保护时间延长。

Abstract

A silane film was formed on LY12 aluminum alloy and the effect of silane pretreatment on the performance of a Mγ-Al rich primer on LY12 alloy were studied. After silane treatment

Si-O-Al covalent bonds were formed between aluminum alloy substrate and silane film and Si-O-Si structure was formed in silane film. In addition

silanol groups -OH in free form and epoxy groups from silane film might react with organic fractions in epoxy coating to form cross-linked bonding

and these two types of groups were bonded through van de Waals force

forming an interpenetrating polymer network (IPN) across the interface and providing improved adhesion between aluminum substrate and silane film. Machu test and electrochemical measurements indicated that silane pre-treatment significantly improved the performance of the Mγ-Al rich primer on LY12 alloy

which was attributed to strengthened barrier effect of the coating system.

关键词

Keywords

references

浏览量

292

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

铝合金表面耐久性超疏水防护膜的制备与表征

涂覆液种类对FeCrAl金属载体上氧化铝涂层性质的影响

无氟无铵铝合金表面预处理新工艺

有机杂环化合物对铝合金在3.5%NaCl介质中的缓蚀作用

无机/有机复合涂层体系在3.5%NaCl溶液中的EIS