- 聚偏氟乙烯/聚二甲基硅氧烷渗透气化膜在丁醇分离中的应用
- Application of polyvinylidene fluoride/polydimethylsiloxane composite membrane in butanol recovery
- 化工学报 2014年第9期页码：3499-3504
- 作者机构：
  
  大连理工大学生命科学与技术学院,辽宁,大连,116023
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.09.026
  中图分类号： 939.9
- 网络首发：2014-09-05，
  
  纸质出版：2014-09-05
- 稿件说明：
移动端阅览
杜广庆, 陈丽杰, 薛闯, 等. 聚偏氟乙烯/聚二甲基硅氧烷渗透气化膜在丁醇分离中的应用[J]. 化工学报, 2014,(9):3499-3504.

DU Guangqing, CHEN Lijie, XUE Chuang, et al. Application of polyvinylidene fluoride/polydimethylsiloxane composite membrane in butanol recovery[J]. CIESC Journal, 2014, (9): 3499-3504.
杜广庆, 陈丽杰, 薛闯, 等. 聚偏氟乙烯/聚二甲基硅氧烷渗透气化膜在丁醇分离中的应用[J]. 化工学报, 2014,(9):3499-3504. DOI： 10.3969/j.issn.0438-1157.2014.09.026.

DU Guangqing, CHEN Lijie, XUE Chuang, et al. Application of polyvinylidene fluoride/polydimethylsiloxane composite membrane in butanol recovery[J]. CIESC Journal, 2014, (9): 3499-3504. DOI： 10.3969/j.issn.0438-1157.2014.09.026.

摘要

通过相转化法制备PVDF多孔支撑膜，在其上涂覆致密的PDMS分离层制备得到PVDF/PDMS复合膜，用于丁醇的分离纯化。以丁醇水溶液为原料液，流速为1.6 L·min-1，丁醇浓度为15 g·L-1，温度为37℃时， PVDF/PDMS复合膜的总通量为158.2 g·m-2·h-1，分离因子为17.3。向丁醇水溶液中按丁醇：丙酮：乙醇比例为6：3：1添加丙酮和乙醇模拟发酵液，PVDF/PDMS复合膜的总通量升高到189.5 g·m-2·h-1，分离因子降低到14.8。进一步考察了以丙酮-丁醇-乙醇（ABE）发酵液为原料液的渗透气化膜分离性能，发酵液中不存在菌体时，PVDF/PDMS复合膜的总通量和分离因子分别为120.2 g·m-2·h-1和19.7，而菌体存在时，复合膜的总通量和分离因子分别为122.1 g·m-2·h-1和16.7。与PDMS均质膜相比，PVDF/PDMS复合膜在丁醇分离过程中的分离性能有了显著的提升，具有潜在的应用价值。

Abstract

A polyvinylidene fluoride (PVDF)/polydimethylsiloxane (PDMS) composite membrane for butanol recovery was fabricated by coating a dense PDMS separation layer on a PVDF porous support layer prepared by phase inversion. The total flux and separation factor of the PVDF/PDMS composite membrane could be 158.2 g·m-2·h-1 and 17.3

respectively

when feed solution was 15 g·L-1 butanol at 37℃ with a flow rate 1.6 L·min-1. To simulate the fermentation liquor

acetone and ethanol were added into the feed solution in a ratio 6(butanol):3:1

the total flux of PVDF/PDMS composite membrane increased to 189.5 g·m-2·h-1

but separation factor decreased to 14.8. Furthermore

fermentation broths with/without biomass as feed solution were investigated to evaluate pervaporation performance of the PVDF/PDMS composite membrane. The total flux and separation factor were 120.2 g·m-2·h-1 and 19.7 for without biomass case

122.1 g·m-2·h-1 and 16.7 for with biomass case

respectively. Compared with PDMS membrane

the performance of PVDF/PDMS composite membrane had significant improvement for butanol recovery

indicating that it is of potential for industrial application of butanol recovery.

关键词

Keywords

references

浏览量

315

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

过渡金属修饰的MoS2催化木质素衍生酚加氢脱氧制备航空燃料芳烃组分

贫氧预处理对生物炭还原NO的影响机制研究

基于多目标优化的航空煤油生物替代燃料模型构建及验证

化学品生物制造过程机器学习的研究进展

温和条件下乙二醇苯醚高效分离回收甘蔗渣组分