稻壳炭基二氧化硅的提取及表征

顾洁; 刘斌; 方放; 马中青; 张齐生; 周建斌

doi:10.3969/j.issn.0438-1157.2014.08.058

您当前的位置：

首页 >

文章列表页 >

稻壳炭基二氧化硅的提取及表征

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 稻壳炭基二氧化硅的提取及表征
- Extraction and characterization of SiO₂ from rice-husk-char
- 化工学报 2014年第8期页码：3277-3282
- 作者机构：
  
  1. 南京林业大学竹材工程研究中心,江苏,南京,210037
  2. 南京林业大学化学工程学院,江苏,南京,210037
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.08.058
  中图分类号： Q127.2
- 网络首发：2014-08-05，
  
  纸质出版：2014-08-05
- 稿件说明：
移动端阅览
顾洁, 刘斌, 方放, 等. 稻壳炭基二氧化硅的提取及表征[J]. 化工学报, 2014,(8):3277-3282.

GU Jie, LIU Bin, FANG Fang, et al. Extraction and characterization of SiO₂ from rice-husk-char[J]. CIESC Journal, 2014, (8): 3277-3282. DOI: 10.3969/j.issn.0438-1157.2014.08.058.
顾洁, 刘斌, 方放, 等. 稻壳炭基二氧化硅的提取及表征[J]. 化工学报, 2014,(8):3277-3282. DOI： 10.3969/j.issn.0438-1157.2014.08.058.

GU Jie, LIU Bin, FANG Fang, et al. Extraction and characterization of SiO₂ from rice-husk-char[J]. CIESC Journal, 2014, (8): 3277-3282. DOI: 10.3969/j.issn.0438-1157.2014.08.058. DOI：

摘要

以气化副产物稻壳炭为原料，以K2CO3作为提取剂制取SiO2产品，考察了提取工艺和陈化工艺对产品得率的影响。得到最优工艺：K2CO3质量分数为20%，浸渍比为3.0，煮溶时间为3.5 h，陈化温度为3℃，陈化时间为3 h。最优工艺下制备的SiO2得率为25.89%，酸处理后纯度为97.02%。采用场发射扫描电子显微镜（SEM）、X射线能谱仪（EDX）、X射线衍射仪（XRD）等对产品的性能进行了表征。

Abstract

The objective of this study is to develop a simple and green procedure for preparing SiO2 from rice husk char. The raw material

rice husk char from downdraft fixed bed gasification was used to extract SiO2 by adding K2CO3. To find the influence of extraction and aging conditions on SiO2 yield

the experiments were conducted. The results showed that the optimum conditions were as follows: the impregnation ratio of K2CO3 solution (mass fraction of 20%) to rice husk char was 3.0

the extraction time 3.5 h. The temperature and time of aging was 3℃ and 3 h

respectively. At these conditions

SiO2 yield was 25.89% and purity 97.02% after acid treatment. The structure and property of SiO2 were analyzed using SEM

EDX

and XRD. The results indicated that it could be a practical way for the high efficiency

environmental-friendly and resource utilization of rice husk char.

关键词

Keywords

references

浏览量

410

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

高灰熔点煤的加压催化气化：K2CO3催化活性及钾回收特性

高Si掺杂RuO2材料的晶体结构、电子结构和导电性

钙基脱硫剂用于冶炼烟气脱硫的模拟与实验

超临界流体干燥技术制备液相色谱填料基质多孔硅球

利用LNG冷能与工业余热的有机朗肯循环复合系统优化分析