炔基腰果酚的制备、表征及其聚合物的非等温固化动力学

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 炔基腰果酚的制备、表征及其聚合物的非等温固化动力学
- Synthesis, characterization of propargyl-cardanol and non-isothermal curing kinetics of its polymer
- 化工学报 2014年第6期页码：2372-2377
- 作者机构：
  
  合肥工业大学化工学院,安徽,合肥,230009
- 作者简介：
  
  吴竞（1987- ），男，硕士研究生
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.06.057
  中图分类号： 631
- 网络首发：2014-06-05，
  
  纸质出版：2014-06-05
- 稿件说明：
移动端阅览
吴竞, 史铁钧, 张方, 等. 炔基腰果酚的制备、表征及其聚合物的非等温固化动力学[J]. 化工学报, 2014,(6):2372-2377.

WU Jing, SHI Tiejun, ZHANG Fang, et al. Synthesis, characterization of propargyl-cardanol and non-isothermal curing kinetics of its polymer[J]. CIESC Journal, 2014, (6): 2372-2377.
吴竞, 史铁钧, 张方, 等. 炔基腰果酚的制备、表征及其聚合物的非等温固化动力学[J]. 化工学报, 2014,(6):2372-2377. DOI： 10.3969/j.issn.0438-1157.2014.06.057.

WU Jing, SHI Tiejun, ZHANG Fang, et al. Synthesis, characterization of propargyl-cardanol and non-isothermal curing kinetics of its polymer[J]. CIESC Journal, 2014, (6): 2372-2377. DOI： 10.3969/j.issn.0438-1157.2014.06.057.

摘要

以3-溴丙炔、腰果酚为原料，利用相转移催化反应合成了炔基化腰果酚树脂，并用FT-IR、1H NMR对炔基化腰果酚的化学结构进行了表征，结果表明在相转移催化剂存在条件下，3-溴丙炔和腰果酚通过Williamson成醚反应成功制备了目标产物。用TG研究固化后的炔基化腰果酚树脂热稳定性能，结果表明，固化后树脂的起始降解温度为419℃，800℃时的残炭率为14%，说明其具有很好的耐热性能。根据DSC曲线，用Kissinger和Flynn-Wall-Ozawa分别计算了热固化反应活化能，分别为143.46 kJ·mol-1和145.15 kJ·mol-1，热固化反应级数都接近1，因此说明这两种模式很适合这种体系。

Abstract

Propargyl cardanol was synthesized using cardanol and propargyl bromide by phase transfer catalyst reaction. The chemical structure of propargyl cardanol was characterized by FT-IR

1H NMR. The results indicated that propargyl cardanol as target compound was obtained through the Williamson ether reaction. Thermal stabilization of poly-propargyl cardanol was evaluated with TG. The initial weight-loss temperature of cured propargyl cardanol was 419℃ and char yield at 800℃ was 14%

which illustrated that the cured propargyl cardano owned well-deserved thermal stability. According to DSC curves

curing kinetic parameters were calculated by two thermo-analysis methods of Kissinger and Flynn-Wall-Ozawa. The respective apparent activation energies were 143.46 and 145.15 kJ·mol-1 respectively and the order of curing reaction both approached to 1

which illustrated that these two kinds of mode were suitable for this system.

关键词

Keywords

references

浏览量

358

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

受鱼脊柱启发的高强韧腰果酚生物基形状记忆环氧树脂

腰果酚生物基自愈合微胶囊的高效制备工艺研究

基于GLAE-MLP的炼化装置管道腐蚀健康状态评估方法

碱金属改性对SrMnO3催化乙苯化学链氧化脱氢性能的影响规律研究

退役光伏组件TPT背板热氧化降解特性研究