Al（OH）<sub>3</sub>胶体的制备及其对铀的吸附机理

张琪; 王清良; 李乾; 胡鄂明; 张洪灿; 杨敬

doi:10.3969/j.issn.0438-1157.2014.04.018

您当前的位置：

首页 >

文章列表页 >

Al（OH）₃胶体的制备及其对铀的吸附机理

分离工程 | 更新时间：2025-12-10

- Al（OH）₃胶体的制备及其对铀的吸附机理
- Preparation of aluminum hydroxide colloid and its adsorption mechanism for uranium(Ⅵ)
- 化工学报 2014年第4期页码：1279-1286
- 作者机构：
  
  1. 南华大学核资源工程学院,湖南,衡阳,421001
  2. 贵州省纳雍县水东中学, 贵州纳雍,553308
- 作者简介：
  
  张琪（1984—），男，硕士研究生.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.04.018
  中图分类号： D868
- 网络首发：2013-11-11，
  
  纸质出版：2013-11-11
- 稿件说明：
移动端阅览
张琪, 王清良, 李乾, 等. Al（OH）₃胶体的制备及其对铀的吸附机理[J]. 化工学报, 2014,(4):1279-1286. DOI: 10.3969/j.issn.0438-1157.2014.04.018.

ZHANG Qi, WANG Qingliang, LI Qian, et al. Preparation of aluminum hydroxide colloid and its adsorption mechanism for uranium(Ⅵ)[J]. CIESC Journal, 2014, (4): 1279-1286.
张琪, 王清良, 李乾, 等. Al（OH）₃胶体的制备及其对铀的吸附机理[J]. 化工学报, 2014,(4):1279-1286. DOI: 10.3969/j.issn.0438-1157.2014.04.018. DOI：

ZHANG Qi, WANG Qingliang, LI Qian, et al. Preparation of aluminum hydroxide colloid and its adsorption mechanism for uranium(Ⅵ)[J]. CIESC Journal, 2014, (4): 1279-1286. DOI： 10.3969/j.issn.0438-1157.2014.04.018.

摘要

为了研究在地浸采铀中胶体对矿层的阻塞及对铀酰离子吸附迁移影响，采用硝酸铝与氨水为原料制备Al（OH）3，并用在pH = 6条件下制备所得的Al（OH）3对铀进行吸附实验研究，考察了吸附的pH值、初始浓度及吸附时间等对Al（OH）3吸附铀的影响。对实验数据使用准一级、复合二级与Elovich 动力学模型进行计算与分析，得出Elovich 动力学方程更适合描述Al（OH）3对铀吸附，吸附主要是表面吸附；使用 Freundlich与Langmuir等温吸附方程对实验数据进行拟合，结果表明Langmuir模型更适合描述Al（OH）3对铀酰离子的吸附；对吸附前、后的Al（OH）3进行SEM与激光粒度分析。

Abstract

In order to study the effect of colloidal seam blocking and adsorption and migration of uranyl ions in situ leaching of uranium

aluminum nitrate and ammonia hydrate were used as the starting materials for preparation of Al(OH)3

and that prepared at pH = 6 was used to adsorb U(Ⅵ) from the solution. The effects of pH value

initial uranium concentration

and contact time on the adsorption were investigated. The pseudo-first-order

composite-second-order and Elovich dynamic models were used to analyze the adsorption data. Freundlich and Langmuir adsorption isotherm models were applied to experimental equilibrium data. The properties of Al(OH)3 were determined by SEM and laser particle size analyzer. The adsorption kinetic parameters obtained shows that the Elovich dynamic model describes the adsorption of uranium on Al(OH)3 colloids well

so the adsorption appears on external surface. The equilibrium data agree well with the Langmuir model.

关键词

Keywords

references

浏览量

440

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

磁性三乙烯四胺氧化石墨烯对Cu2+的吸附行为

甲基丙烯酸接枝改性玉米芯对Cd2+的吸附及机理

温度敏感聚N-异丙基丙烯酰胺/谷氨酸钠/壳聚糖复合材料制备及吸附性能研究

ZIF-8基多孔液体制备及其SO2吸附性能

碳负载硒掺杂硫化钴在锂硫电池中的性能研究

Al（OH）3胶体的制备及其对铀的吸附机理

Preparation of aluminum hydroxide colloid and its adsorption mechanism for uranium(Ⅵ)

DOI：10.3969/j.issn.0438-1157.2014.04.018

摘要

Abstract

关键词

Keywords

references

Al（OH）₃胶体的制备及其对铀的吸附机理