丙烯醇催化氨化合成3-甲基吡啶催化剂的制备及性能

催化、动力学与反应器 | 更新时间：2025-12-10

- 丙烯醇催化氨化合成3-甲基吡啶催化剂的制备及性能
- Preparation and performance of Zn/H-ZSM-5 catalyst for catalytic amination of allyl alcohol to 3-picoline
- 化工学报 2014年第3期页码：905-911
- 作者机构：
  
  河北工业大学化工学院,天津,300130
- 作者简介：
  
  马天奇（1989—），男，硕士研究生.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2014.03.020
  中图分类号： TQ032.4}
- 网络首发：2014-03-05，
  
  纸质出版：2014-03-05
- 稿件说明：
移动端阅览
马天奇, 魏天宇, 骈岩杰, 等. 丙烯醇催化氨化合成3-甲基吡啶催化剂的制备及性能[J]. 化工学报, 2014,(3):905-911.

MA Tianqi, WEI Tianyu, PIAN Yanjie, et al. Preparation and performance of Zn/H-ZSM-5 catalyst for catalytic amination of allyl alcohol to 3-picoline[J]. CIESC Journal, 2014, (3): 905-911.
马天奇, 魏天宇, 骈岩杰, 等. 丙烯醇催化氨化合成3-甲基吡啶催化剂的制备及性能[J]. 化工学报, 2014,(3):905-911. DOI： 10.3969/j.issn.0438-1157.2014.03.020.

MA Tianqi, WEI Tianyu, PIAN Yanjie, et al. Preparation and performance of Zn/H-ZSM-5 catalyst for catalytic amination of allyl alcohol to 3-picoline[J]. CIESC Journal, 2014, (3): 905-911. DOI： 10.3969/j.issn.0438-1157.2014.03.020.

摘要

采用浸渍法制备了一系列H-ZSM-5分子筛负载过渡金属锌催化剂，在固定床反应器上考察了这些催化剂对丙烯醇催化氨化合成3-甲基吡啶的催化性能。通过对H-ZSM-5的硅铝比、锌负载量对催化剂催化性能影响的考察，发现硅铝比为80、锌负载量为12%时得到的催化剂Zn12/H-ZSM-5（80）的催化性能最佳。在常压、反应温度420℃、氨醇摩尔比3：1、空速300 h-1条件下，丙烯醇在该催化剂上的转化率和3-甲基吡啶的选择性分别达到97.8%和37.9%。利用X射线衍射（XRD）、X射线光电子能谱（XPS）以及吡啶吸附红外对催化剂进行了表征，结果表明，Zn12/H-ZSM-5（80）上负载的Zn2+为L酸；在丙烯醇生成3-甲基吡啶的反应过程中催化剂的脱氢活性物种为氧化锌，而加成和环合反应则主要是由催化剂中的L酸催化实现的。

Abstract

H-ZSM-5 supported zinc catalysts were prepared by impregnation method

and their catalytic performances for amination of allyl alcohol to 3-picoline were evaluated in a fixed-bed reactor. It is found that the catalyst Zn12/H-ZSM-5(80) (H-ZSM-5 with 80 silicon/aluminum (Si/Al) ratio and zinc loading of 12%) shows the best performance among all the studied catalysts. 97.8% conversion of allyl alcohol and 37.9% selectivity toward 3-picoline are obtained on this catalyst using reaction conditions: atmospheric pressure

at 420℃

ammonia/allyl alcohol mole ratio 3:1 and gas hour space velocity 300 h-1. The characterization results

obtained by X-ray diffraction (XRD)

X-ray photoelectron spectroscopy (XPS) and FT-IR of absorbed pyridine

indicate that zinc on Zn12/H-ZSM-5(80) is Zn2+

there is Lewis acid on HZSM-5. In 3-picoline formation

ZnO provides active sites of dehydrogenation reaction

and addition and cyclization reactions are mainly catalyzed by the Lewis acid.

关键词

Keywords

references

浏览量

364

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

ZSM-5/EU-1共生分子筛的可控合成及催化裂解性能

ZSM-5分子筛上轻烃裂解性能:晶粒尺寸的影响

Ca（OH）2/CaO间接反应器储释热循环性能优化

机器学习辅助快速筛选高性能CO2吸附分子筛

高分散双位点Co物种协同催化CO2氧化乙烷脱氢制乙烯的研究