离子液体-水体系循环使用对白松木质素提取的影响

项婧; 李坤兰; 魏立纲; 马英冲; 张倩; 李慧; 王奥博; 高明; 王磊; 邱慧慧

doi:10.3969/j.issn.0438-1157.2013.z1.018

您当前的位置：

首页 >

文章列表页 >

离子液体-水体系循环使用对白松木质素提取的影响

分离工程 | 更新时间：2025-12-10

- 离子液体-水体系循环使用对白松木质素提取的影响
- Effect of recycle of ionic liquid on its performance of white pine lignin extraction
- 化工学报 2013年第S1期页码：124-127
- 作者机构：
  
  大连工业大学轻工与化学工程学院,辽宁,大连,116034
- 作者简介：
  
  项婧(1989—)，女，硕士研究生.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.z1.018
  中图分类号： 645TQ35
- 网络首发：2013-12-30，
  
  纸质出版：2013-12-30
- 稿件说明：
移动端阅览
项婧, 李坤兰, 魏立纲, 等. 离子液体-水体系循环使用对白松木质素提取的影响[J]. 化工学报, 2013,(S1):124-127.

ZHANG Qian, LI Hui, WEI Ligang, et al. Effect of recycle of ionic liquid on its performance of white pine lignin extraction[J]. CIESC Journal, 2013, (S1): 124-127.
项婧, 李坤兰, 魏立纲, 等. 离子液体-水体系循环使用对白松木质素提取的影响[J]. 化工学报, 2013,(S1):124-127. DOI： 10.3969/j.issn.0438-1157.2013.z1.018.

ZHANG Qian, LI Hui, WEI Ligang, et al. Effect of recycle of ionic liquid on its performance of white pine lignin extraction[J]. CIESC Journal, 2013, (S1): 124-127. DOI： 10.3969/j.issn.0438-1157.2013.z1.018.

摘要

使用氯代丁基咪唑盐离子液体的水溶液分离白松中的木质素。在[C4min]Cl/H2O质量比为6∶4，混合液与白松质量比为10∶1，提取温度150℃下，提取白松木质素。离子液体-水可多次循环用于提取白松木质素，溶剂体系循环使用对木屑失重率、木屑残渣综纤维素含量和离子液体木质素提取率均有影响。通过UV和FT-IR分析提取物的结构，并与磨木木素比较，证明提取物中有木质素的特征官能团。通过SEM分析观察提取木质素前后木屑表面的变化，发现提取后木屑表面出现了大量纹孔，纹孔膜消失。

Abstract

This paper investigated the recycling of ionic liquid-[Bmim]Cl in the extraction of white pine lignin. The extraction condition as following: the ratio of solvent to pine powder was 10∶1

ionic liquid concentration was 60%

the extraction is at 150℃ for 2 h. The results showed that ionic liquid could be recycled after the extraction of white pine lignin

but the sawdust mass loss

the holocellulose content in the residue wood chip and ionic liquid lignin extraction rate were all influenced by the recycling of the solvents. The UV and FT-IR spectrum were used to determine the chemical structure of the extraction materials. Through the comparison with mill wood lignin

there exist characteristic functional groups of lignin. The SEM analysis was used to investigate the surface change of the wood before and after extraction

which show a lot of sawdust pits on the surface

along with the disappearance of pit membranes.

关键词

Keywords

references

浏览量

556

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

稻壳炭基二氧化硅的提取及表征

木质素结构以及表面活性剂对木质素吸附纤维素酶的影响

GeCl4-MxCly-H2体系下锗-杂质竞争沉积热力学研究

富氧空位锌掺杂PdO/ZrO2催化CO2和苯酚合成碳酸二苯酯

部分预混旋流燃烧入口激励下的熵波产生及耗散机制研究