质子化处理改性黏土制备NBRCNs的结构与性能

梁玉蓉; 谭英杰; 王林艳; 李培杰; 胡刚; 段学召

doi:10.3969/j.issn.0438-1157.2013.10.050

您当前的位置：

首页 >

文章列表页 >

质子化处理改性黏土制备NBRCNs的结构与性能

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 质子化处理改性黏土制备NBRCNs的结构与性能
- Structure and properties of NBRCNs prepared from protonated octadecyl amine modified clay
- 化工学报 2013年第10期页码：3858-3864
- 作者机构：
  
  太原工业学院材料工程系,山西,太原,030008
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.10.050
  中图分类号： Q330.1
- 网络首发：2013-10-05，
  
  纸质出版：2013-10-05
- 稿件说明：
移动端阅览
梁玉蓉, 谭英杰, 王林艳, 等. 质子化处理改性黏土制备NBRCNs的结构与性能[J]. 化工学报, 2013,(10):3858-3864.

LIANG Yurong, TAN Yingjie, WANG Linyan, et al. Structure and properties of NBRCNs prepared from protonated octadecyl amine modified clay[J]. CIESC Journal, 2013, (10): 3858-3864.
梁玉蓉, 谭英杰, 王林艳, 等. 质子化处理改性黏土制备NBRCNs的结构与性能[J]. 化工学报, 2013,(10):3858-3864. DOI： 10.3969/j.issn.0438-1157.2013.10.050.

LIANG Yurong, TAN Yingjie, WANG Linyan, et al. Structure and properties of NBRCNs prepared from protonated octadecyl amine modified clay[J]. CIESC Journal, 2013, (10): 3858-3864. DOI： 10.3969/j.issn.0438-1157.2013.10.050.

摘要

采用经质子化处理后的十八烷基胺改性黏土制备丁腈橡胶/黏土纳米复合材料(NBRCNs)。旨在获得具有更大晶层间距结构的有机黏土(OC)(XRD测试)

削弱黏土片层之间的界面作用力

将黏土片层以纳米尺寸均匀分散在NBR中(SEM、TEM表征)

最终获得具有优异力学性能的 NBRCNs。实验结果表明

当有机黏土含量为10phr时

采用经质子化处理后的十八烷基胺改性黏土制备NBRCNs的拉伸强度、撕裂强度、100%/300%定伸应力及硬度

与采用常规的长链脂肪族季铵盐改性有机黏土制备的NBR/C16-OC纳米复合材料和NBR/S18-OC纳米复合材料相比

分别提高了61.04%、51.79%、30%/26.21%、7.27%和80.28%、49.57%、31.09%/34.72%、11.32%。

Abstract

NBRCNs was prepared by mixing nitrile butadiene rubber with protonated octadecyl amine modified clay to further expand the layer space and weaken the layer-layer interaction.Attributed to greatly improved dispersion uniformity of silicate layers

the prepared nanocomposites by protonated octadecyl amine modified clay demonstrated superior properties to those of nanocomposites prepared by the traditional long chain aliphatic quaternary amine modified clay.Compared with NBR/C16-OC and NBR/S18-OC nanocomposites

NBRCNs with 10phr loading of protonated octadecyl amine modified clay exhibited about 61.04% and 80.28% increase in tensile strength

51.79% and 49.57% increase in tear strength

30%/26.21% and 31.09%/34.72% increase in 100%/300% stress

and 7.27% and 11.32% increase in Shore A hardness.

关键词

Keywords

references

浏览量

200

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

溶剂对丁腈橡胶溶解、尺寸、结构和催化加氢的影响研究

石墨烯/聚苯胺修饰阳极对微生物燃料电池性能的影响

聚丙烯基高含量埃洛石纳米管复合材料的制备和性能

微滴乳液聚合制备PDMS/SiO2纳米复合材料

高性能丁基橡胶/有机黏土纳米复合材料的新型制备方法