- 机械活化淀粉制备水凝胶及其尿素的控释性
- Preparation of mechanically activated starch-based composite hydrogel for controlled release of urea
- 化工学报 2013年第9期页码：3428-3436
- 作者机构：
  
  1. 钦州学院化学化工学院,广西,钦州,535000
  2. 广西大学化学化工学院,广西,南宁,530004
  3. 广西化工研究院,广西,南宁,530001
- 作者简介：
  
  梁兴唐(1982- ),男,讲师.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.09.047
  中图分类号： Q326.4TQ449+.1
- 网络首发：2013-09-05，
  
  纸质出版：2013-09-05
- 稿件说明：
移动端阅览
梁兴唐, 胡华宇, 张燕娟, 等. 机械活化淀粉制备水凝胶及其尿素的控释性[J]. 化工学报, 2013,(9):3428-3436.

LIANG Xingtang, HU Huayu, ZHANG Yanjuan, et al. Preparation of mechanically activated starch-based composite hydrogel for controlled release of urea[J]. CIESC Journal, 2013, (9): 3428-3436.
梁兴唐, 胡华宇, 张燕娟, 等. 机械活化淀粉制备水凝胶及其尿素的控释性[J]. 化工学报, 2013,(9):3428-3436. DOI： 10.3969/j.issn.0438-1157.2013.09.047.

LIANG Xingtang, HU Huayu, ZHANG Yanjuan, et al. Preparation of mechanically activated starch-based composite hydrogel for controlled release of urea[J]. CIESC Journal, 2013, (9): 3428-3436. DOI： 10.3969/j.issn.0438-1157.2013.09.047.

摘要

以机械活化60 min的木薯淀粉、氢氧化钾部分中和的丙烯酸和丙烯酰胺为原料

合成农用淀粉基离子/非离子型复合高吸水树脂(SCSA)

采用FT-IR和SEM对样品的官能团和表面形貌进行表征。以SCSA在5.0 mol·L-1的尿素溶液中平衡溶胀后所得的水凝胶(SCH)为尿素在水溶液中的释放材料

考察合成工艺条件和释放环境对尿素释放过程的影响。结果表明

尿素从SCH中的释放过程符合Fickian扩散机理;SCH的溶胀率越大

尿素的释放速率越慢;释放温度越高

尿素的释放越快。在丙烯酸和丙烯酰胺质量比为3:3

交联剂N

N'-亚甲基双丙烯酰胺溶液用量为1.0 ml(浓度为0.02 mol·L-1)的条件下制备的SCH对尿素的释放活化能为17.28 kJ·mol-1。

Abstract

The starch based ionic and nonionic composite superabsorbent(SCSA)used for agriculture was synthesized from mechanically activated cassava starch(60 min ball milling)

partially neutralized acrylic acid by KOH and acrylamide.The functional groups and granular morphology of the samples were characterized by FT-IR and SEM

respectively.The SCSA was swollen in urea solution(5.0 mol·L-1)until equilibrium swelling and then the hydrogel(SCH)was obtained.The SCH was used as the release material for urea in aqueous solution.The effects of synthesis conditions and release environment on the release process were investigated.It was found that the release of urea from SCH was controlled by Fickian diffusion mechanism

and the release rate decreased with increasing swelling ratio and increased with increasing temperature.The activation energy for releasing urea from the SCH prepared under the conditions of mAA:mAM=3:3 and dosage of N

N'-methylenebisacrylamide solution 1.0 ml(0.02 mol·L-1)was 17.28 kJ·mol-1.

关键词

Keywords

references

浏览量

238

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

液相法合成三聚氰酸体系热力学分析

基于分子筛绿色合成的天然硅铝矿物介尺度活化研究进展

秸秆烘焙过程氯、硫释放及AAEMs迁徙转化特性研究

尿素和二甲基亚砜诱导DhaA变性的分子动力学模拟

铬铁矿无钙焙烧渣的SO2还原解毒