氧化石墨烯对SiO<sub>2</sub>多孔陶瓷吸波性能的影响

张国英; 梁文阁

doi:10.3969/j.issn.0438-1157.2013.07.052

您当前的位置：

首页 >

文章列表页 >

氧化石墨烯对SiO₂多孔陶瓷吸波性能的影响

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 氧化石墨烯对SiO₂多孔陶瓷吸波性能的影响
- Effects of graphene oxide on electromagnetic wave absorption properties of porous silica ceramic
- 化工学报 2013年第7期页码：2696-2700
- 作者机构：
  
  1. 浙江商业职业技术学院,浙江,杭州,310053
  2. 山西省焦炭集团公司,山西,太原,030024
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.07.052
  中图分类号： Q028
- 网络首发：2013-07-05，
  
  纸质出版：2013-07-05
- 稿件说明：
移动端阅览
张国英, 梁文阁. 氧化石墨烯对SiO₂多孔陶瓷吸波性能的影响[J]. 化工学报, 2013,(7):2696-2700. DOI: 10.3969/j.issn.0438-1157.2013.07.052.

ZHANG Guoying, LIANG Wenge. Effects of graphene oxide on electromagnetic wave absorption properties of porous silica ceramic[J]. CIESC Journal, 2013, (7): 2696-2700.
张国英, 梁文阁. 氧化石墨烯对SiO₂多孔陶瓷吸波性能的影响[J]. 化工学报, 2013,(7):2696-2700. DOI: 10.3969/j.issn.0438-1157.2013.07.052. DOI：

ZHANG Guoying, LIANG Wenge. Effects of graphene oxide on electromagnetic wave absorption properties of porous silica ceramic[J]. CIESC Journal, 2013, (7): 2696-2700. DOI： 10.3969/j.issn.0438-1157.2013.07.052.

摘要

采用颗粒堆积法

以石英砂为骨料

甲基纤维素为黏结剂干压成型后

在1300℃保温1 h烧结制备得到SiO2多孔陶瓷样品。通过对样品吸波性能的测试

发现样品的吸波带较宽达到9 GHz

反射率约-3 dB。经过浸渍氧化石墨烯后

样品的吸波性能发生较大改变。在氧化石墨烯质量分数为0.004%时

由于氧化石墨烯的涡流损耗

样品的吸波性能较纯SiO2多孔陶瓷样品的吸波性能提高75%

反射率达到-5 dB。过量的氧化石墨烯使多孔陶瓷样品呈现出对电磁波的全反射。

Abstract

A particle packing method was developed to prepare porous silica ceramics aggregated by sintering silica powder with methyl cellulose as binding agent at 1300℃ for 1 h.The result of electromagnetic wave absorption showed obvious electromagnetic wave absorption properties with a bandwidth of 9 GHz and-3 dB reflectivity.The electromagnetic wave absorption properties changed after graphene oxide (GO)layers were incorporated into the samples.When the mass fraction of graphene oxide impregnated samples was 0.004%

an increase of 75% in absorption was observed with the greatest reflectivity of-5 dB.The eddy current damping caused by these GO layers was responsible for the enhanced absorption efficiency.While excess GO made the porous sample to be a reflector for incident waves.

关键词

Keywords

references

浏览量

371

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

石墨烯增强的生物炭/正十八烷定型复合相变材料制备及性能研究

硼掺杂氮基石墨烯检测变压器油中溶解气体CO和CO2的密度泛函理论研究

碳纳米材料在锌离子电池中的应用研究进展

加热表面材质对核态沸腾换热影响的流-热耦合数值研究

基于3D打印的多孔陶瓷膜研究进展

氧化石墨烯对SiO2多孔陶瓷吸波性能的影响

Effects of graphene oxide on electromagnetic wave absorption properties of porous silica ceramic

DOI：10.3969/j.issn.0438-1157.2013.07.052

摘要

Abstract

关键词

Keywords

references

氧化石墨烯对SiO₂多孔陶瓷吸波性能的影响