TiO<sub>2</sub>载体特性对二苯并噻吩加氢脱硫性能的影响

汪怀远; 朱友庄; 赵景岩; 程小双; 张志华

doi:10.3969/j.issn.0438-1157.2013.07.021

您当前的位置：

首页 >

文章列表页 >

TiO₂载体特性对二苯并噻吩加氢脱硫性能的影响

催化、动力学与反应器 | 更新时间：2025-12-10

- TiO₂载体特性对二苯并噻吩加氢脱硫性能的影响
- Effect of characteristics of TiO₂ carrier on performance of dibenzothiophene hydrodesulfurization
- 化工学报 2013年第7期页码：2462-2467
- 作者机构：
  
  1. 东北石油大学化学化工学院,黑龙江,大庆,163318
  2. 大庆化工研究中心,黑龙江,大庆,163318
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.07.021
  中图分类号： 643.3
- 网络首发：2013-07-05，
  
  纸质出版：2013-07-05
- 稿件说明：
移动端阅览
汪怀远, 朱友庄, 赵景岩, 等. TiO₂载体特性对二苯并噻吩加氢脱硫性能的影响[J]. 化工学报, 2013,(7):2462-2467. DOI: 10.3969/j.issn.0438-1157.2013.07.021.

WANG Huaiyuan, ZHU Youzhuang, ZHAO Jingyan, et al. Effect of characteristics of TiO₂ carrier on performance of dibenzothiophene hydrodesulfurization[J]. CIESC Journal, 2013, (7): 2462-2467. DOI: 10.3969/j.issn.0438-1157.2013.07.021.
汪怀远, 朱友庄, 赵景岩, 等. TiO₂载体特性对二苯并噻吩加氢脱硫性能的影响[J]. 化工学报, 2013,(7):2462-2467. DOI: 10.3969/j.issn.0438-1157.2013.07.021. DOI：

WANG Huaiyuan, ZHU Youzhuang, ZHAO Jingyan, et al. Effect of characteristics of TiO₂ carrier on performance of dibenzothiophene hydrodesulfurization[J]. CIESC Journal, 2013, (7): 2462-2467. DOI: 10.3969/j.issn.0438-1157.2013.07.021. DOI：

摘要

以自制的大比表面介孔二氧化钛晶须作为加氢脱硫催化剂的载体

采用一步浸渍法制备了MoO3-NiO/TiO2催化剂

并用 X 射线衍射、N2 吸附-脱附、SEM、拉曼衍射等技术对载体和催化剂进行了表征

考察了TiO2晶须材料作为二苯并噻吩(DBT)上加氢脱硫(HDS)催化剂载体的性能及优越性

并详细考察了不同TiO2载体的晶型与比表面积对催化剂加氢脱硫反应活性的影响。结果表明

TiO2介孔晶须具有较为活泼的锐钛矿相和晶须形貌

同时提供了大的比表面积和特殊的孔道结构

在温度280℃、氢分压2.0 MPa、氢/油体积比400、体积空速4 h-1的温和条件下

DBT转化率即可接近100%。比表面积相近时

催化剂的脱硫效果依次为锐钛矿相>混晶>金红石相;同为锐钛矿相TiO2载体

催化剂的脱硫效果随着比表面的增大而增加。

Abstract

An attempt using self-regulating mesoporous titanium dioxide whisker as catalyst carrier of hydrogen desulfurization

was carried out to prepare MoO3-NiO/TiO2 catalyst by single-step incipient wetness impregnation.X-ray

N2 absorption/desorption

SEM

Raman diffraction were adopted to characterize the carrier and catalyst.The effect of mesoporous TiO2 whisker as catalyst carrier on the performance of dibenzothiophene (DBT)hydrogen desulfurization (HDS)was evaluated.The results showed that the mesoporous TiO2 whisker had highly active anatase

whisker morphology and larger specific surface area as well as special pore structure.DBT conversion over mesoporous TiO2 whisker could approach 100% under moderate conditions of reaction temperature 280℃

hydrogen partial pressure 2.0 MPa

hydrogen/oil volume ratio 400 and LHSV 4 h-1.Under the condition of similar specific surface area

the sequence of the desulfurization effect of the tested catalysts was anatase> mixed crystals of TiO2 >rutile.As anatase carriers are concerned

the desulfurization effect increased with the increase of the specific surface area of TiO2 carrier.

关键词

Keywords

references

浏览量

563

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

B2O3负载量对MoO3/CeO2-Al2O3耐硫甲烷化性能的影响

WO3/TiO2-ZrO2脱硝催化剂制备及其NH3活化机理

负载[APMIm][Br]离子液体吸收CO2的性能

流化床CVD法原位合成CNTs-Ni-TiO2及其光催化性能

甘油中水合TiO2及不同晶型纳米TiO2光致变色现象

TiO2载体特性对二苯并噻吩加氢脱硫性能的影响

Effect of characteristics of TiO2 carrier on performance of dibenzothiophene hydrodesulfurization

DOI：10.3969/j.issn.0438-1157.2013.07.021

摘要

Abstract

关键词

Keywords

references

TiO₂载体特性对二苯并噻吩加氢脱硫性能的影响

Effect of characteristics of TiO₂ carrier on performance of dibenzothiophene hydrodesulfurization