三聚氰胺改性木质素的制备及银离子吸附性能

王文栋; 张健伟; 郑积烽; 吕秋丰

doi:10.3969/j.issn.0438-1157.2013.04.049

您当前的位置：

首页 >

文章列表页 >

三聚氰胺改性木质素的制备及银离子吸附性能

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 三聚氰胺改性木质素的制备及银离子吸附性能
- Preparation of melamine-modified lignin and its adsorption performance for silver ion
- 化工学报 2013年第4期页码：1478-1484
- 作者机构：
  
  福州大学材料科学与工程学院,福建,福州,350116
- 作者简介：
  
  王文栋(1991—),男,本科.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.04.049
  中图分类号： Q317TQ319
- 网络首发：2013-04-05，
  
  纸质出版：2013-04-05
- 稿件说明：
移动端阅览
王文栋, 张健伟, 郑积烽, 等. 三聚氰胺改性木质素的制备及银离子吸附性能[J]. 化工学报, 2013,(4):1478-1484.

WANG Wendong, ZHANG Jianwei, ZHENG Jifeng, et al. Preparation of melamine-modified lignin and its adsorption performance for silver ion[J]. CIESC Journal, 2013, (4): 1478-1484.
王文栋, 张健伟, 郑积烽, 等. 三聚氰胺改性木质素的制备及银离子吸附性能[J]. 化工学报, 2013,(4):1478-1484. DOI： 10.3969/j.issn.0438-1157.2013.04.049.

WANG Wendong, ZHANG Jianwei, ZHENG Jifeng, et al. Preparation of melamine-modified lignin and its adsorption performance for silver ion[J]. CIESC Journal, 2013, (4): 1478-1484. DOI： 10.3969/j.issn.0438-1157.2013.04.049.

摘要

以酶解木质素、三聚氰胺和甲醛为原料

通过接枝反应制备三聚氰胺改性酶解木质素(MEHL)

并研究MEHL对银离子的吸附性能。接枝反应的研究结果表明

三聚氰胺和甲醛的添加量对产率有很大影响。酶解木质素、三聚氰胺、甲醛质量比为10:6:6

于90℃下反应4 h

所制得的MEHL的产率可达83.7%。红外光谱、热重和元素分析的结果表明

三聚氰胺成功接枝到酶解木质素分子上。MEHL的含氮量由酶解木质素的0.81%提高到18.55%。银离子的吸附研究表明

MEHL对银离子表现出很好的吸附性能。在银离子初始浓度为0.16 mol·L-1

在MEHL用量为50 mg

吸附温度为30℃时吸附36 h

MEHL对银离子的吸附容量为944.1 mg·g-1。

Abstract

Melamine-modified lignin (MEHL) was prepared using grafting reaction from hydrolyzed lignin (EHL) by enzyme

melamine and formaldehyde

and its adsorption for silver ions was studied.The results from grafting reaction showed that content of melamine and formaldehyde had great influences on MEHL yield.High yield 83.7% for MEHL was achieved with EHL:melamine:formaldehyde mass ratio 10:6:6 at reaction temperature 90℃ and reaction time 4 h.The MEHL obtained was characterized by FTIR

TGA and elemental analysis.The results showed that melamine molecules had been grafted onto EHL chains.Nitrogen content in MEHL had obvious increase from original 0.81% to 18.55%.Furthermore

the adsorption performance for silver ions at the same conditions was much stronger for MEHL than for EHL.Its maximum adsorption capacity was up to 944.1 mg·g-1 at optimal conditions:50 mg MEHL

initial silver ion concentration 0.16 mol·L-1

30℃ and 36 h.

关键词

Keywords

references

浏览量

392

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

木质素羟丙基磺甲基化改性及其对纤维素酶水解的影响

一步法制备富氧木质素活性炭及其亚甲基蓝吸附性能

木质素的化学改性及其对AuCl4-的吸附

羧甲基化碱木质素对农药的吸附分散作用机理

菜籽秆预处理废液再生木质素对镉铅离子的吸附性能