微滴乳液聚合制备PDMS/SiO<sub>2</sub>纳米复合材料

杨磊; 许湧深; 邱守季; 张娅

doi:10.3969/j.issn.0438-1157.2013.04.048

您当前的位置：

首页 >

文章列表页 >

微滴乳液聚合制备PDMS/SiO₂纳米复合材料

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 微滴乳液聚合制备PDMS/SiO₂纳米复合材料
- Preparation of PDMS/SiO₂ nanocomposites via miniemulsion polymerization
- 化工学报 2013年第4期页码：1473-1477
- 作者机构：
  
  天津大学化工学院,天津,300072
- 作者简介：
  
  杨磊(1989—),男,硕士研究生.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.04.048
  中图分类号： 635
- 网络首发：2013-04-05，
  
  纸质出版：2013-04-05
- 稿件说明：
移动端阅览
杨磊, 许湧深, 邱守季, 等. 微滴乳液聚合制备PDMS/SiO₂纳米复合材料[J]. 化工学报, 2013,(4):1473-1477. DOI: 10.3969/j.issn.0438-1157.2013.04.048.

YANG Lei, XU Yongshen, QIU Shouji, et al. Preparation of PDMS/SiO₂ nanocomposites via miniemulsion polymerization[J]. CIESC Journal, 2013, (4): 1473-1477. DOI: 10.3969/j.issn.0438-1157.2013.04.048.
杨磊, 许湧深, 邱守季, 等. 微滴乳液聚合制备PDMS/SiO₂纳米复合材料[J]. 化工学报, 2013,(4):1473-1477. DOI: 10.3969/j.issn.0438-1157.2013.04.048. DOI：

YANG Lei, XU Yongshen, QIU Shouji, et al. Preparation of PDMS/SiO₂ nanocomposites via miniemulsion polymerization[J]. CIESC Journal, 2013, (4): 1473-1477. DOI: 10.3969/j.issn.0438-1157.2013.04.048. DOI：

摘要

采用超声分散的方法

以少量八甲基环四硅氧烷(D4)对硅溶胶粒子进行表面接枝改性。然后在改性硅溶胶存在下

以十二烷基苯磺酸(DBSA)为乳化剂兼催化剂进行D4的微滴乳液聚合

得到聚硅氧烷(PDMS)/二氧化硅(SiO2)纳米复合乳液。采用FTIR、TGA、纳米粒度仪、TEM和拉力机分别对样品进行了表征。结果表明:采用超声分散的方法

能够有效地实现硅溶胶粒子的表面改性。通过微滴乳液聚合得到的复合乳胶粒是聚合物包覆二氧化硅粒子的核壳结构形态。SiO2的引入提高了有机硅复合膜力学性能

增强了热稳定性。

Abstract

Ultrasonic dispersion process was utilized to modify silica sol nanoparticles with a small amount of D4.Then in the presence of modified silica sol

miniemulsion polymerization of D4 was conducted with DBSA as emulsifier and catalyst

and polydimethylsiloxane(PDMS)/SiO2 nanocomposites emulsion latex was obtained.Modified silica sol particles were characterized by FTIR and TGA.The diameter and morphology of the composite latex particles were analyzed by nano particle size analyzer and TEM

respectively.Mechanical properties and thermal stability of the composite films were characterized by tensile test and TGA.The results showed that ultrasonic dispersion was an effective way to modify silica sol particles.Modified silica sol particles could be encapsulated by polydimethylsiloxane and form core-shell latex particle morphology during miniemulsion polymerization.Introduction of SiO2 improved mechanical properties and thermal stabilities of polysiloxane composite films.

关键词

Keywords

references

浏览量

420

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

SiO2溶胶在微滴乳液聚合中的原位纳米复合

α， ω-端羟基苯基/亚苯基高乙烯基聚硅氧烷的合成及热稳定性

三维网络萃取膜的制备及传质效率研究

石墨烯/聚苯胺修饰阳极对微生物燃料电池性能的影响

多壁碳纳米管/二氧化硅纳米复合材料的制备及其吸油性能

微滴乳液聚合制备PDMS/SiO2纳米复合材料

Preparation of PDMS/SiO2 nanocomposites via miniemulsion polymerization

DOI：10.3969/j.issn.0438-1157.2013.04.048

摘要

Abstract

关键词

Keywords

references

微滴乳液聚合制备PDMS/SiO₂纳米复合材料

Preparation of PDMS/SiO₂ nanocomposites via miniemulsion polymerization