PFSA-PES-纳米颗粒复合纳米纤维的制备及催化性能

陆培培; 许振良; 杨虎; 马晓华; 魏永明

doi:10.3969/j.issn.0438-1157.2013.04.047

您当前的位置：

首页 >

文章列表页 >

PFSA-PES-纳米颗粒复合纳米纤维的制备及催化性能

材料化学工程与纳米技术 | 更新时间：2025-12-10

- PFSA-PES-纳米颗粒复合纳米纤维的制备及催化性能
- Preparation of perfluorosulfonic acid-polyethersulfone-nanoparticles composite nanofibers and their catalytic properties
- 化工学报 2013年第4期页码：1466-1472
- 作者机构：
  
  华东理工大学化学工程联合国家重点实验室,化学工程研究所膜科学与工程研发中心,上海,200237
- 作者简介：
  
  陆培培(1986—),男,博士研究生.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.04.047
  中图分类号： Q31
- 网络首发：2013-04-05，
  
  纸质出版：2013-04-05
- 稿件说明：
移动端阅览
陆培培, 许振良, 杨虎, 等. PFSA-PES-纳米颗粒复合纳米纤维的制备及催化性能[J]. 化工学报, 2013,(4):1466-1472.

LU Peipei, XU Zhenliang, YANG Hu, et al. Preparation of perfluorosulfonic acid-polyethersulfone-nanoparticles composite nanofibers and their catalytic properties[J]. CIESC Journal, 2013, (4): 1466-1472.
陆培培, 许振良, 杨虎, 等. PFSA-PES-纳米颗粒复合纳米纤维的制备及催化性能[J]. 化工学报, 2013,(4):1466-1472. DOI： 10.3969/j.issn.0438-1157.2013.04.047.

LU Peipei, XU Zhenliang, YANG Hu, et al. Preparation of perfluorosulfonic acid-polyethersulfone-nanoparticles composite nanofibers and their catalytic properties[J]. CIESC Journal, 2013, (4): 1466-1472. DOI： 10.3969/j.issn.0438-1157.2013.04.047.

摘要

利用静电纺丝法制备了全氟磺酸(PFSA)-聚醚砜(PES)-纳米颗粒(SiO2、TiO2和Al2O3)复合纳米纤维

比较了SiO2、TiO2和Al2O3等不同纳米颗粒对磺酸基团在纤维表面分布的影响

并利用乙酸乙酯合成反应考察了纤维结构对表面磺酸基团活性的关系。结果表明:静电纺复合纳米纤维的比表面积可达85.6 m2·g-1

纳米颗粒均匀分布在纤维表面

表面酸性中心占PFSA酸性基团总量最高达71.2%。酯化反应实验表明

复合纳米纤维具有很好的催化性能

纳米颗粒的存在可以提高酸中心的活性;同时

所得复合纳米纤维膜表现出很好的回收与可再生性能

有望作为一种对环境友好的固体酸催化剂。

Abstract

Nanofibers of perfluorosulfonic acid (PFSA)

polyethersulfone (PES) and nanoparticles (SiO2

TiO2 and Al2O3) were prepared by electrospinning method from PFSA-PES-nanoparticle suspensions.The effects of nanoparticles on morphology and surface acid groups of thenanofibers were investigated.The composite nanofibers were tested in esterification of acetic acid (HAc) and ethanol (EtOH) to investigate the relationship between structures and catalytic performance.The results showed that the specific surface area of obtained nanofibers was 85.6 m2穏-1.Nanoparticles were well distributed on the surface of the nanofibers and provided enough surface area for the reactants.The number of surface acidic centers on the surface was 71.2% of total PFSA acidic groups.Besides

the nanofibers exhibited good catalytic performance in the reactions due to improvement of activity by the nanoparticles.Moreover

these fibers could be well recovered and regenerated

and could be used as an environmental-friendly solid acid catalyst.

关键词

Keywords

references

浏览量

246

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

TiO2-V2O5纳米纤维光催化氧化烟气中的Hg0

二维纳米片增强间位芳纶纳米纤维及其阻燃性能研究

纳米颗粒吸附界面对微孔喉中液滴运移及堵塞的调控

静电纺丝纳米纤维双疏膜油性细颗粒物过滤性能实验分析

纤维状BPO4/SiO2催化剂的制备及其丙烷氧化脱氢性能