- 停机过程中锅炉高温受热面蒸汽侧氧化膜的应力分析
- Numerical analysis of stresses of steam-side oxide scales in boiler high-temperature heating surface in shutdown process
- 化工学报 2013年第4期页码：1444-1452
- 作者机构：
  
  1. 南京工程学院能源与动力工程学院,江苏,南京,211167
  2. 东南大学能源与环境学院,江苏,南京,210096
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.04.044
  中图分类号： K223
- 网络首发：2013-04-05，
  
  纸质出版：2013-04-05
- 稿件说明：
移动端阅览
边彩霞, 周克毅, 朱正林, 等. 停机过程中锅炉高温受热面蒸汽侧氧化膜的应力分析[J]. 化工学报, 2013,(4):1444-1452.

BIAN Caixia, ZHOU Keyi, ZHU Zhenglin, et al. Numerical analysis of stresses of steam-side oxide scales in boiler high-temperature heating surface in shutdown process[J]. CIESC Journal, 2013, (4): 1444-1452.
边彩霞, 周克毅, 朱正林, 等. 停机过程中锅炉高温受热面蒸汽侧氧化膜的应力分析[J]. 化工学报, 2013,(4):1444-1452. DOI： 10.3969/j.issn.0438-1157.2013.04.044.

BIAN Caixia, ZHOU Keyi, ZHU Zhenglin, et al. Numerical analysis of stresses of steam-side oxide scales in boiler high-temperature heating surface in shutdown process[J]. CIESC Journal, 2013, (4): 1444-1452. DOI： 10.3969/j.issn.0438-1157.2013.04.044.

摘要

电站锅炉高温受热面蒸汽侧氧化膜在机组停机降负荷时可能发生脱落

对安全性构成严重威胁。通过建立有限元分析模型

对锅炉停机过程中受热面蒸汽侧氧化膜内的应力进行了计算和分析。对铁素体合金和奥氏体合金进行了研究

其中铁素体合金以T91为代表

奥氏体合金以TP347H为代表。通过对各应力分量以及von Mises等效应力进行分析

揭示机组降负荷过程中两种合金管蒸汽侧氧化膜内应力的变化规律

阐明两种合金管蒸汽侧氧化膜可能的失效模式

同时得出了铁素体合金管和奥氏体合金管蒸汽侧氧化膜分别在负荷降低后期和初期容易发生脱落的结论。

Abstract

Exfoliation of steam-side oxide scale in heating surface occurring during load reduction severely affects the safety of thermal power plants.Through building the finite element model for steady stress analysis

the stresses in steam-side oxide scales during unit load drop were calculated and analyzed.Ferrite alloy represented by T91 and austenitic alloy represented by TP347H were investigated in this paper. Through analyzing each of the stress components and the von Mises equivalent stress

the change of the stresses in steam-side oxide scales for both ferrite alloy and austenitic alloy during unit load drop was revealed.The possible failure modes of steam-side oxide scales for both alloys were illustrated

and it could also be concluded that the exfoliation of steam-side oxide scales for ferrite alloy and austenitic alloy was more liable to occur in the final stage and in the initial stage of load reduction respectively.

关键词

Keywords

references

浏览量

325

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

HVOF喷涂用于提高锅炉换热面耐磨损耐腐蚀性能综述

纤维水膜极板表面颗粒沉积脱落特性

机械密封覆层密封环端面性能分析

基于气/液相法的中空纤维无泡曝气膜传氧性能

基于时序-空间双流卷积神经网络的炼化污水厂进水COD预测模型