Ni-Sn-P合金镀层在人工海水中的腐蚀行为及腐蚀机理

王宏智; 吴强; 张智贤; 姚素微; 张卫国

doi:10.3969/j.issn.0438-1157.2013.04.032

您当前的位置：

首页 >

文章列表页 >

Ni-Sn-P合金镀层在人工海水中的腐蚀行为及腐蚀机理

表面与界面工程 | 更新时间：2025-12-10

- Ni-Sn-P合金镀层在人工海水中的腐蚀行为及腐蚀机理
- Corrosion behavior and mechanism of Ni-Sn-P alloy coatings in artificial sea water
- 化工学报 2013年第4期页码：1359-1363
- 作者机构：
  
  天津大学化工学院,天津,300072
- 作者简介：
  
  王宏智(1973—),男,副教授,博士.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.04.032
  中图分类号： 646.6
- 网络首发：2013-04-05，
  
  纸质出版：2013-04-05
- 稿件说明：
移动端阅览
王宏智, 吴强, 张智贤, 等. Ni-Sn-P合金镀层在人工海水中的腐蚀行为及腐蚀机理[J]. 化工学报, 2013,(4):1359-1363.

WANG Hongzhi, WU Qiang, ZHANG Zhixian, et al. Corrosion behavior and mechanism of Ni-Sn-P alloy coatings in artificial sea water[J]. CIESC Journal, 2013, (4): 1359-1363.
王宏智, 吴强, 张智贤, 等. Ni-Sn-P合金镀层在人工海水中的腐蚀行为及腐蚀机理[J]. 化工学报, 2013,(4):1359-1363. DOI： 10.3969/j.issn.0438-1157.2013.04.032.

WANG Hongzhi, WU Qiang, ZHANG Zhixian, et al. Corrosion behavior and mechanism of Ni-Sn-P alloy coatings in artificial sea water[J]. CIESC Journal, 2013, (4): 1359-1363. DOI： 10.3969/j.issn.0438-1157.2013.04.032.

摘要

利用扫描电子显微镜(SEM)和能谱(EDS)测试了电镀Ni-Sn-P合金镀层在人工海水中腐蚀前后表面形貌和合金成分的变化

结合X射线光电子能谱(XPS)对腐蚀后合金表面的组成进行了分析

并在此基础上探讨了Ni-Sn-P合金镀层在人工海水中的腐蚀机理。研究结果表明:电镀Ni-Sn-P合金在人工海水中耐蚀性优于Ni-P合金

由于人工海水中的氯离子的穿透效应而出现的局部腐蚀孔数较Ni-P合金大幅减少

腐蚀后Ni-Sn-P合金表面形成由SnO2、SnCl4、Ni3(PO4)2、NiO和Ni(OH)2组成的膜层

对合金耐蚀性的提高起到重要作用。

Abstract

The changes of microscopic morphology and elemental composition of Ni-Sn-P alloy coatings before and after corrosion in artificial sea water were studied with scanning electron microscopy (SEM) and energy dispersive spectrometer (EDS)

and the corrosion products were examined with X-ray photoelectron spectroscopy (XPS).The corrosion mechanism of Ni-Sn-P alloy coatings in artificial sea water is discussed.EIS spectra and SEM showed that the corrosion resistance of electroplating Ni-Sn-P alloy in artificial seawater was better than Ni-P alloy

and the number of localized corrosion hole caused by penetration effect of Cl- was greatly reduced.After corrosion a layer of passive film composed of SnO2

SnCl4

Ni3(PO4)2

NiO and Ni(OH)2 was formed on the surface of Ni-Sn-P alloy

which played an important role in improving Ni-Sn-P alloy coatings corrosion resistance.

关键词

Keywords

references

浏览量

405

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

基于GLAE-MLP的炼化装置管道腐蚀健康状态评估方法

机器学习在结晶过程建模与控制中的研究进展

部分预混旋流燃烧入口激励下的熵波产生及耗散机制研究

GeCl4-MxCly-H2体系下锗-杂质竞争沉积热力学研究

电子效应精准调控的纳米金催化剂在低碳多元醇选择性氧化研究进展