室温自交联功能单体N,N'-二双丙酮丙酰胺基乙二胺的合成与应用

陈德海; 孙东成

doi:10.3969/j.issn.0438-1157.2013.03.046

您当前的位置：

首页 >

文章列表页 >

室温自交联功能单体N,N'-二双丙酮丙酰胺基乙二胺的合成与应用

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 室温自交联功能单体N,N'-二双丙酮丙酰胺基乙二胺的合成与应用
- Synthesis and application of EDA-di(diacetone propionamido) in room temperature self-crosslinking
- 化工学报 2013年第3期页码：1112-1117
- 作者机构：
  
  华南理工大学化学与化工学院,广东,广州,510640
- 作者简介：
  
  陈德海(1987—),男,硕士研究生.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.03.046
  中图分类号： Q323.8
- 网络首发：2013-03-05，
  
  纸质出版：2013-03-05
- 稿件说明：
移动端阅览
陈德海, 孙东成. 室温自交联功能单体N,N'-二双丙酮丙酰胺基乙二胺的合成与应用[J]. 化工学报, 2013,(3):1112-1117.

CHEN Dehai, SUN Dongcheng. Synthesis and application of EDA-di(diacetone propionamido) in room temperature self-crosslinking[J]. CIESC Journal, 2013, (3): 1112-1117.
陈德海, 孙东成. 室温自交联功能单体N,N'-二双丙酮丙酰胺基乙二胺的合成与应用[J]. 化工学报, 2013,(3):1112-1117. DOI： 10.3969/j.issn.0438-1157.2013.03.046.

CHEN Dehai, SUN Dongcheng. Synthesis and application of EDA-di(diacetone propionamido) in room temperature self-crosslinking[J]. CIESC Journal, 2013, (3): 1112-1117. DOI： 10.3969/j.issn.0438-1157.2013.03.046.

摘要

利用乙二胺与双丙酮丙烯酰胺间的Michael加成反应合成了含酮羰基的新型扩链剂N

N'-二双丙酮丙酰胺基乙二胺

用1H NMR和13C MNR证实了结构。聚己二酸新戊二醇酯、异佛尔酮二异氰酸酯(IPDI)、二羟甲基丙酸(DMPA)预聚后加入N

N'-二双丙酮丙酰胺基乙二胺扩链得到含酮聚氨酯预聚物

预聚物经分散、乙二胺扩链后得到聚氨酯分散体。研究了含酮扩链剂用量对分散体及其膜性能的影响。结果表明随N

N'-二双丙酮丙酰胺基乙二胺的增加

聚氨酯分散体的粒径增大、黏度减小。己二酸二酰肼交联后能明显提高WPU胶膜的力学性能。

Abstract

A new type of comonomer EDA-di(diacetone propionamido) was synthesized by the Michael addition reaction using diacetone acrylamide and ethanediamine as raw materials.The structure of the monomer was verified by 1H NMR and 13C MNR.Polyurethane dispersions(PUDs) were synthesized by the prepolymerization process using polyneopentanediol adipate(PNA) as soft segment

isophorone diisocyanate(IPDI) as hard segment

dimethylolpropionic acid(DMPA) as hydrophilic monomer

EDA-di(diacetone propionamido) as functional monomer.Research was done to know the influence of monomer on polyurethane dispersions.The result showed that particle size increased as the content of monomer increased while viscosity decreased.The mechanical property was improved through the room temperature self-crosslinking of adipic dihydrazide(ADH).

关键词

Keywords

references

浏览量

449

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

磷酸钒锂正极材料的氮掺杂碳包覆与Ti4+共掺杂协同改性研究

塔式太阳能辅助超临界压缩CO2储能系统热力学性能

硫基光催化剂在高效光催化制氢中研究进展

机器学习在结晶过程建模与控制中的研究进展

微波强化焦化废盐中有机物脱除性能研究