- 丙烯超临界聚合中原生晶特征
- Crystallographic behavior of nascent isotactic polypropylene produced under supercritical conditions
- 化工学报 2013年第2期页码：730-734
- 作者机构：
  
  1. 浙江大学化工系聚合与聚合物工程研究所,浙江,杭州,310027
  2. 化学工程联合国家重点实验室(浙江大学),浙江,杭州,310027
  3. 中国石化扬子石油化工有限公司研究院,江苏,南京,210048
- 作者简介：
  
  邱少龙(1987—),男,硕士研究生.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.02.044
  中图分类号： Q325
- 网络首发：2013-02-05，
  
  纸质出版：2013-02-05
- 稿件说明：
移动端阅览
邱少龙, 霍志宏, 曹堃, 等. 丙烯超临界聚合中原生晶特征[J]. 化工学报, 2013,(2):730-734.

QIU Shaolong, HUO Zhihong, CAO Kun, et al. Crystallographic behavior of nascent isotactic polypropylene produced under supercritical conditions[J]. CIESC Journal, 2013, (2): 730-734.
邱少龙, 霍志宏, 曹堃, 等. 丙烯超临界聚合中原生晶特征[J]. 化工学报, 2013,(2):730-734. DOI： 10.3969/j.issn.0438-1157.2013.02.044.

QIU Shaolong, HUO Zhihong, CAO Kun, et al. Crystallographic behavior of nascent isotactic polypropylene produced under supercritical conditions[J]. CIESC Journal, 2013, (2): 730-734. DOI： 10.3969/j.issn.0438-1157.2013.02.044.

摘要

通过广角X射线衍射(WAXD)对由丙烯超临界聚合和传统本体淤浆法制得的等规聚丙烯原生结晶特征进行了研究

并讨论了聚合工艺、预聚温度、粒径、分子量等对原生晶特征的影响。结果表明

超临界聚合法制备的等规聚丙烯(SC-iPP)呈现出α和γ的混合晶型

而采用传统淤浆法制备的等规聚丙烯(C-iPP)只含有单一α晶型

这是因为超临界的高温高压状态

使得体系传热传质阻力较小

更有利于原生晶型的发展。此外

预聚温度、粒径、分子量等因素也对丙烯超临界聚合所制得的SC-iPP结晶特征有显著影响。

Abstract

The materials used here were isotactic polypropylene (iPP) produced by conventional slurry polymerization and under supercritical conditions.Wide-angle X-ray diffraction (WAXD) patterns of the iPPs obtained under various conditions were recorded to analyze the nascent polymorphic form.The effects of polymerization process

pre-polymerization temperature

particle size and molecular weight of the resultant iPPs on nascent polymorphic form were investigated.The iPP produced by supercritical polymerization was the mixture of α and γ forms while the iPP produced by conventional slurry process was only in the α form

just because

in the supercritical state of high pressure and high temperature

mass and heat transfer should be faster

which would facilitate development of nascent polymorphic form. Furthermore

pre-polymerization temperature

particle size and molecular weight of obtained iPPs were found to have significant effect on nascent crystallographic behavior.

关键词

Keywords

references

浏览量

391

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

预接触温度对聚丙烯DQC球形催化剂聚合性能的影响

剪切历史对微注塑制品形态结构和力学性能的影响

基于递归特性和CNN的上升管内气液两相流型识别研究

不同SK型静态混合器的流场特性及其混合效果分析

原位水热法可控合成Bi2MoO6/MoO3复合纤维及其高效光催化产氢性能