高黏度、高热稳定性羧甲基淀粉己酸酯的溶液性质

汪源浩; 具本植; 张淑芬

doi:10.3969/j.issn.0438-1157.2013.01.030

您当前的位置：

首页 >

文章列表页 >

高黏度、高热稳定性羧甲基淀粉己酸酯的溶液性质

热力学 | 更新时间：2025-12-10

- 高黏度、高热稳定性羧甲基淀粉己酸酯的溶液性质
- Aqueous solution properties of carboxymethyl starch hexanoate with high viscosity and thermal stability
- 化工学报 2013年第1期页码：275-282
- 作者机构：
  
  大连理工大学精细化工国家重点实验室,辽宁,大连,116024
- 作者简介：
  
  汪源浩(1981—),男,博士研究生.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2013.01.030
  中图分类号： Q314.1O623.54
- 网络首发：2013-01-05，
  
  纸质出版：2013-01-05
- 稿件说明：
移动端阅览
汪源浩, 具本植, 张淑芬. 高黏度、高热稳定性羧甲基淀粉己酸酯的溶液性质[J]. 化工学报, 2013,(1):275-282.

WANG Yuanhao, JU Benzhi, ZHANG Shufen. Aqueous solution properties of carboxymethyl starch hexanoate with high viscosity and thermal stability[J]. CIESC Journal, 2013, (1): 275-282.
汪源浩, 具本植, 张淑芬. 高黏度、高热稳定性羧甲基淀粉己酸酯的溶液性质[J]. 化工学报, 2013,(1):275-282. DOI： 10.3969/j.issn.0438-1157.2013.01.030.

WANG Yuanhao, JU Benzhi, ZHANG Shufen. Aqueous solution properties of carboxymethyl starch hexanoate with high viscosity and thermal stability[J]. CIESC Journal, 2013, (1): 275-282. DOI： 10.3969/j.issn.0438-1157.2013.01.030.

摘要

以羧甲基淀粉(CMS)为原料制备了高黏度、高热稳定性的羧甲基淀粉己酸酯(CMSH)。用IR和TG对产物进行了结构和热稳定性质研究;通过Brookfield R/S-CC流变仪对羧甲基淀粉己酸酯溶液黏度性质和影响因素

如己酰基质量分数、浓度、剪切力、温度及溶液黏度的剪切恢复性质、温度敏感性质等进行了详细研究。结果表明

引入己酰基基团后

可以降低黏度对温度的敏感性

显著提高羧甲基淀粉的热稳定性和溶液的黏度值。但己酰基团的引入

不能提高CMS溶液黏度的抗剪切性和剪切恢复性。当己酰基质量分数为11.8%时

羧甲基淀粉己酸酯的初始热分解温度由260℃提高到300℃;溶液的黏度值由420 mPa·s提高到32000 mPa·s。

Abstract

Carboxymethyl starch hexanoate (CMSH) with high viscosity and thermal stability was prepared by esterification of carboxymethyl starch (CMS).The chemical structure and thermal stability were characterized by IR and TG.The relative hysteresis area

temperature sensitivity and factors affecting viscosity of CMSH

such as mass percentage of hexyl (MPhexyl)

concentration

shear rate and temperature

were studied using Brookfield R/S-CC Rheometer.The result indicates that temperature sensitivity

thermal stability and viscosity can be improved by introducing hexyls into CMS.Initial decomposition temperature(IDT)of CMSH increased from 260℃ to 300℃

the viscosity was also increased when compared with CMS because of the hydrophobic aggregation of hexyls

and the viscosity value reached 32000 mPa·s at MPhexyl of 11.8%.However

the shear resistance and the relative hysteresis area can not be improved by introduction of hexyl group.

关键词

Keywords

references

浏览量

390

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

水溶性聚合物型稠油降黏剂研究进展

R513A与PVE润滑油的溶解度及黏度研究

NdF3含量对NdF3-LiF熔盐局域结构和输运性质的影响

基于联邦学习的聚酯纤维酯化过程温度预测研究

咪唑二氰胺离子液体掺混糠醇的自燃及推进性能