高比表面磁性有序介孔炭的合成及对亚甲基蓝的吸附性能

田勇; 钟国英; 王秀芳; 林汉森

doi:10.3969/j.issn.0438-1157.2012.12.049

您当前的位置：

首页 >

文章列表页 >

高比表面磁性有序介孔炭的合成及对亚甲基蓝的吸附性能

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 高比表面磁性有序介孔炭的合成及对亚甲基蓝的吸附性能
- Preparation of high specific surface area magnetic ordered mesoporous carbons and adsorption property of methylene blue
- 化工学报 2012年第12期页码：4082-4088
- 作者机构：
  
  广东药学院药科学院,广东,广州,510006
- 作者简介：
  
  田勇(1977-),男,博士,副教授.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.12.049
  中图分类号： 647TQ424.1
- 网络首发：2012-12-05，
  
  纸质出版：2012-12-05
- 稿件说明：
移动端阅览
田勇, 钟国英, 王秀芳, 等. 高比表面磁性有序介孔炭的合成及对亚甲基蓝的吸附性能[J]. 化工学报, 2012,(12):4082-4088.

TIAN Yong, ZHONG Guoying, WANG Xiufang, et al. Preparation of high specific surface area magnetic ordered mesoporous carbons and adsorption property of methylene blue[J]. CIESC Journal, 2012, (12): 4082-4088.
田勇, 钟国英, 王秀芳, 等. 高比表面磁性有序介孔炭的合成及对亚甲基蓝的吸附性能[J]. 化工学报, 2012,(12):4082-4088. DOI： 10.3969/j.issn.0438-1157.2012.12.049.

TIAN Yong, ZHONG Guoying, WANG Xiufang, et al. Preparation of high specific surface area magnetic ordered mesoporous carbons and adsorption property of methylene blue[J]. CIESC Journal, 2012, (12): 4082-4088. DOI： 10.3969/j.issn.0438-1157.2012.12.049.

摘要

具有高比表面积、大孔容的铁磁性有序介孔炭(Fe/OMCs)对含染料废水的处理提供了一种简单有效的方法。采用苯酚树脂作炭源

三嵌段共聚物F127为模板剂

正硅酸乙酯为硅前驱体

硝酸铁为磁源

通过软模路线合成了Fe/OMCs。利用X射线衍射仪(XRD)

氮气吸附仪

透射电镜(TEM)和综合物性测试仪研究了硝酸铁加入量对Fe/OMCs的相态、孔结构参数和磁性的影响;并以亚甲基蓝(MB)为染料探针分子

研究了Fe/OMCs对MB的吸附行为。结果表明材料有序性、比表面和孔容随着硝酸铁加入量的增加而降低

而饱和磁化强度明显增强。Fe/OMCs对MB有快速吸附能力

其行为符合Sips吸附方程。

Abstract

Magnetic Fe-containing ordered mesoporous carbons(Fe/OMCs)with high surface area and large pore volume provide an easy and effective way for the treatment of dye in waste water.Fe/OMCs were synthesized by the soft-template route

wherein phenolic resin was used as a carbon precursor

triblock copolymer F127 as a template agent

tetraethylorsilicate(TEOS)as a silica precursor and hydrated iron nitrate as an iron source.The effects of Fe(NO3)3?9H2O loading on the morphology

structural parameters

and magnetic properties of the Fe/OMCs were evaluated by X-ray diffraction(XRD)

N2 sorption analysis

transmission electron microscopy(TEM)and physical property measurements.By using methylene blue(MB)as model dye

the adsorption of MB on the obtained Fe/OMCs was investigated.The experimental results showed that the ordering

specific surface area and total pore volume decreased with the increase of Fe(NO3)3?9H2O loading.The Fe/OMCs had fast adsorption ability for MB.The adsorption of MB on the obtained Fe/OMCs followed the Sips adsorption equation and the corresponding parameters were obtained.

关键词

Keywords

references

浏览量

217

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

一步法制备富氧木质素活性炭及其亚甲基蓝吸附性能

双金属硫化物CuCo2S4的合成及其在锂硫电池中的应用

氧缺陷位MoO3-x的制备及其吸附性能研究

超声波辅助粉煤灰去除水中亚甲基蓝染料的动力学分析

锰氧化物材料的制备及应用进展