- Electro-catalytic dechlorination performance of LaNi₅ hydrogen storage electrode modified by palladium
- 化工学报 2012年第12期页码：3882-3888
- 作者机构：
  
  浙江工业大学生物与环境工程学院,浙江,杭州,310032
- 作者简介：
  
  何志桥(1973-),男,副教授.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.12.021
  中图分类号： 646X703
- 网络首发：2012-07-17，
  
  纸质出版：2012-07-17
- 稿件说明：
移动端阅览
何志桥, 林科吉, 陈建孟, 等. Pd修饰LaNi₅贮氢电极的电催化脱氯性能[J]. 化工学报, 2012,(12):3882-3888. DOI: 10.3969/j.issn.0438-1157.2012.12.021.

HE Zhiqiao, LIN Keji, CHEN Jianmeng, et al. Electro-catalytic dechlorination performance of LaNi₅ hydrogen storage electrode modified by palladium[J]. CIESC Journal, 2012, (12): 3882-3888. DOI: 10.3969/j.issn.0438-1157.2012.12.021.
何志桥, 林科吉, 陈建孟, 等. Pd修饰LaNi₅贮氢电极的电催化脱氯性能[J]. 化工学报, 2012,(12):3882-3888. DOI: 10.3969/j.issn.0438-1157.2012.12.021. DOI：

HE Zhiqiao, LIN Keji, CHEN Jianmeng, et al. Electro-catalytic dechlorination performance of LaNi₅ hydrogen storage electrode modified by palladium[J]. CIESC Journal, 2012, (12): 3882-3888. DOI: 10.3969/j.issn.0438-1157.2012.12.021. DOI：

摘要

为提高对氯苯酚(4-CP)脱氯的有效性

采用化学沉积法制备了镧镍合金镀钯电极(Pd/LaNi5)

对其进行了X射线衍射(XRD)、扫描电子显微镜(SEM)和线性扫描伏安(LSV)表征。电催化实验结果表明Pd/LaNi5电极显示了比LaNi5电极和Pd/Ni电极更高的4-CP脱氯活性

在初始浓度0.1 mmol·L-1、表观电流密度10 mA·cm-2、pH 4.0和钯载量1.8 mg·cm-2时

4-CP的脱氯率和电流效率分别达到77.3%和0.14%。基于物理化学表征

可以断定电化学脱氯活性的增强主要源于LaNi5更好的储氢能力。

Abstract

To improve dechlorination effectiveness of 4-chlorophenol

palladium-modified lanthanum-nickel electrode(Pd/LaNi5 electrode)was prepared by chemical deposition

and characterized by X-ray diffraction(XRD)

scanning electron microscopy(SEM)and linear sweep voltammetry(LSV).The measurement results of electrocatalytic activity show that the dechlorination efficiency is higher for Pd/LaNi5 electrode than for LaNi5 and Pd/Ni electrode.At conditions of 4-CP initial concentration 0.1 mmol稬-1

apparent current density 10 mA穋m-2

pH 4.0 and Pd loading 1.8 mg穋m-2

the dechlorination efficiency was 77.3%

and corresponding current efficiency 0.14%. Based on the physico-chemical characterization

the conclusion is that better hydrogen-storage property of LaNi5 is responsible for the enhancement of electrochemical dechlorination process.

关键词

Keywords

references

浏览量

269

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

锂离子电池水性黏结剂的改性策略及应用研究进展

硫化物电解质的界面调控及研究进展

锂离子电池电极中多级孔道结构设计

电化学合成氨研究进展

烟气脱硫过程含硫量自适应预测与异常状态溯源方法

Pd修饰LaNi5贮氢电极的电催化脱氯性能

Electro-catalytic dechlorination performance of LaNi5 hydrogen storage electrode modified by palladium

DOI：10.3969/j.issn.0438-1157.2012.12.021

摘要

Abstract

关键词

Keywords

references

Pd修饰LaNi₅贮氢电极的电催化脱氯性能

Electro-catalytic dechlorination performance of LaNi₅ hydrogen storage electrode modified by palladium