磷钨酸盐催化转化葡萄糖合成乙酰丙酸

曾珊珊; 林鹿; 刘娣; 彭林才

doi:10.3969/j.issn.0438-1157.2012.12.020

您当前的位置：

首页 >

文章列表页 >

磷钨酸盐催化转化葡萄糖合成乙酰丙酸

催化、动力学与反应器 | 更新时间：2025-12-10

- 磷钨酸盐催化转化葡萄糖合成乙酰丙酸
- Catalytic conversion of glucose to levulinic acid by solid heteropolyacid salts
- 化工学报 2012年第12期页码：3875-3881
- 作者机构：
  
  1. 华南理工大学制浆造纸工程国家重点实验室,广东,广州,510640
  2. 厦门大学能源研究院,福建,厦门,361005
- 作者简介：
  
  曾珊珊(1987-),女,硕士研究生.
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.12.020
  中图分类号： Q032.41
- 网络首发：2012-07-17，
  
  纸质出版：2012-07-17
- 稿件说明：
移动端阅览
曾珊珊, 林鹿, 刘娣, 等. 磷钨酸盐催化转化葡萄糖合成乙酰丙酸[J]. 化工学报, 2012,(12):3875-3881.

ZENG Shanshan, LIN Lu, LIU Di, et al. Catalytic conversion of glucose to levulinic acid by solid heteropolyacid salts[J]. CIESC Journal, 2012, (12): 3875-3881.
曾珊珊, 林鹿, 刘娣, 等. 磷钨酸盐催化转化葡萄糖合成乙酰丙酸[J]. 化工学报, 2012,(12):3875-3881. DOI： 10.3969/j.issn.0438-1157.2012.12.020.

ZENG Shanshan, LIN Lu, LIU Di, et al. Catalytic conversion of glucose to levulinic acid by solid heteropolyacid salts[J]. CIESC Journal, 2012, (12): 3875-3881. DOI： 10.3969/j.issn.0438-1157.2012.12.020.

摘要

制备了一系列金属离子修饰的磷钨酸盐(MXH3-2XPW12O40

M=Zn

Ag)催化剂

并将磷钨酸银盐(Ag3PW12O40)用于水解葡萄糖制备乙酰丙酸的实验中。采用FTIR、XRD、SEM和EPMA等技术对磷钨酸盐性能进行了表征

并分析了磷钨酸银盐催化剂在反应前后结构和表面元素相对含量的变化。考察了反应温度、反应时间、催化剂用量和葡萄糖浓度等对乙酰丙酸得率的影响。结果表明:合成的磷钨酸盐具有磷钨酸的Keggin结构

并且Ag3PW12O40催化剂在多次使用后Keggin结构没有被破坏。在催化合成反应中

在反应温度200℃、反应时间2 h、Ag3PW12O40催化剂用量0.7 g和葡萄糖浓度40 g·L-1的条件下

乙酰丙酸的最大得率可达到81.61%

催化剂可重复利用。

Abstract

A series of metal-modified heteropolyacid salt catalysts(MXH3-2XPW12O40

M=Zn

Ag)were prepared

and the solid heteropolyacid salt Ag3W12O40 was used in hydrolysis of glucose to produce levulinic acid.The surface structures of different heteropolyacid salt catalysts were characterized by means of FTIR

XRD.The surface structures and element relative mass content change of the fresh and used Ag3W12O40 catalyst were also analyzed by means of FTIR

XRD

SEM and EPMA.The effects of such factors as reaction temperature

reaction time

amount of catalyst and glucose concentration on the yield of levulinic acid were investigated.Experimental results showed that the MXH3-2XPW12O40 heteropolyacid salt catalysts kept primary Keggin structure

and Ag3W12O40 catalyst had the structure of Keggin after reuse for several times.It was found that the highest yield of levulinic acid was 81.61%(mole) under the conditions of reaction temperature 200℃

reaction time 2 h

Ag3PW12O40 catalyst dosage 0.7 g and glucose concentration 40 g·L-1.The catalyst could be used repeatedly.

关键词

Keywords

references

浏览量

407

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

L酸/B酸可调的磺酸功能化MIL-101(Cr)材料催化葡萄糖脱水制备5-羟甲基糠醛

混合酸催化葡萄糖选择性转化合成乙酰丙酸甲酯

过渡金属基氮掺杂炭的构筑及其脱硫性能研究

复合金属CuCr2O4表面CNCl水解反应机理

过渡金属修饰的MoS2催化木质素衍生酚加氢脱氧制备航空燃料芳烃组分