- 室温交联聚丙烯酸酯乳胶膜的制备及其渗透性能
- Preparation and permeability of ambient crosslinking polyacrylate latex film
- 化工学报 2012年第7期页码：2279-2284
- 作者机构：
  
  福州大学化学化工学院
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.07.042
  中图分类号： Q337;TQ028
- 网络首发：2012-07-05，
  
  纸质出版：2012-07-05
- 稿件说明：
移动端阅览
林美娜. 室温交联聚丙烯酸酯乳胶膜的制备及其渗透性能[J]. 化工学报, 2012,(7):2279-2284.

林美娜. Preparation and permeability of ambient crosslinking polyacrylate latex film[J]. CIESC Journal, 2012, (7): 2279-2284.
林美娜. 室温交联聚丙烯酸酯乳胶膜的制备及其渗透性能[J]. 化工学报, 2012,(7):2279-2284. DOI： 10.3969/j.issn.0438-1157.2012.07.042.

林美娜. Preparation and permeability of ambient crosslinking polyacrylate latex film[J]. CIESC Journal, 2012, (7): 2279-2284. DOI： 10.3969/j.issn.0438-1157.2012.07.042.

摘要

以双丙酮丙烯酰胺（DAAM）为官能性单体合成了带酮羰基的聚丙烯酸酯核壳乳液，将其与己二酸二酰肼（ADH）在室温下交联制备了聚丙烯酸酯多孔乳胶膜，考察了乳液壳层组成、ADH用量、致孔剂用量及种类对乳胶膜渗透性能的影响。研究结果表明，当壳层组成BA/(MMA+AA+DAAM)质量比为2.5/2.5时，乳胶粒子没有完全变形，粒子间相互融接堆积，结合致孔剂的作用，形成了内部呈疏松多孔结构的乳胶膜，膜的渗透量较高；研究进一步揭示，限制大分子链段的热运动有利于维持乳胶膜的多孔结构，从而获得较高的渗透量；此外，发现以葡萄糖、聚乙二醇300（PEG300）为致孔剂时可使乳胶膜获得较高的渗透量。

Abstract

Taking adipic acid dihydrazide (ADH)as cross-linker

a porous polyacrylate latex film was formed at ambient temperature from polyacrylate core-shell emulsion incorporated with diacetone acrylamide (DAAM).The effects of shell composition of core-shell emulsion

ADH content

porogen content and porogen type on the permeability of latex film were investigated.The results showed that the latex particles with BA/(MMA+AA+DAAM)=2.5/2.5（mass ratio） in shell composition could not fuse completely into a continuous dense film

but formed granular deposits.Then

a loose and porous latex film with high permeability was formed with the help of porogen.The investigation further revealed that the restricted movement of polymer chains contributed to the maintenance of porous structure in the latex film and then high permeability.In addition

the study indicated that the latex films with high permeability were formed with glucose or polyethylene glycol (PEG300)as porogen.

关键词

Keywords

references

浏览量

474

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

聚酰亚胺膜材料分子结构设计强化CO2渗透性研究进展

面向不同工业二氧化碳分离体系的膜材料研究进展

聚丙烯酸酯/铜酞菁蓝复合乳胶膜中颜料颗粒的分散状态

钙循环热化学储能载能体放热特性研究

带束层结构设计对全钢子午线轮胎硫化特性的影响