- Research and characterization of ethylene-propylene rubber modified by in-situ sol-gel method
- 化工学报 2012年第7期页码：2266-2270
- 作者机构：
  
  天津大学化工学院
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.07.040
  中图分类号： B324
- 网络首发：2012-07-05，
  
  纸质出版：2012-07-05
- 稿件说明：
移动端阅览
党帅营. 原位溶胶-凝胶法改性EPDM及其表征[J]. 化工学报, 2012,(7):2266-2270.

党帅营. Research and characterization of ethylene-propylene rubber modified by in-situ sol-gel method[J]. CIESC Journal, 2012, (7): 2266-2270.
党帅营. 原位溶胶-凝胶法改性EPDM及其表征[J]. 化工学报, 2012,(7):2266-2270. DOI： 10.3969/j.issn.0438-1157.2012.07.040.

党帅营. Research and characterization of ethylene-propylene rubber modified by in-situ sol-gel method[J]. CIESC Journal, 2012, (7): 2266-2270. DOI： 10.3969/j.issn.0438-1157.2012.07.040.

摘要

采用原位溶胶-凝胶反应制备乙丙橡胶/ SiO2纳米复合材料。分别以乙丙橡胶（EPDM）和γ-甲基丙烯酰氧丙基三甲氧基硅烷（KH570）接枝改性的乙丙橡胶（EPDM-g-KH570）在前驱体四乙氧基硅烷（TEOS）中溶胀，再浸入含有正丁胺的催化剂溶液中催化前驱体的原位溶胶-凝胶反应。考察了不同溶剂以及催化剂含量对TEOS转化率和原位生成的SiO2粒径的影响。采用FT-IR、SEM等测试手段对纳米复合材料进行了表征。结果表明，接枝KH570后，TEOS转化率明显提高，SiO2粒径明显减小，在材料中的分散性很好。

Abstract

Ethylene-propylene diene monomer rubber-g-γ-methacryloxypropyltrimethoxysilane (EPDM-g-KH570)/SiO2 nanocomposites were prepared with the in-situ sol-gel method.Firstly

the EPDM-g-KH570 was prepared by co-irradiation.Then the graft product was soaked into tetraethylorthosilicate (TEOS).Finally

the swollen material was put into butylamine solution to catalyze the sol-gel reaction of the precursor TEOS.The influences of different solvents and concentrations of butylamine on sol-gel reaction of TEOS and the particle size of the silica obtained were studied.The morphology and microstructures of EPDM-g-KH570/SiO2 hybrid were characterized by FT-IR and SEM.The results showed that the swelling of TEOS and the equilibrium conversion of TEOS were improved significantly by grafted KH570. Compared to the ungrafted EPDM

SiO2 average diameters were smaller and had a good dispersion in the grafted EPDM.

关键词

Keywords

references

浏览量

331

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

退役光伏组件TPT背板热氧化降解特性研究

Ca（OH）2/CaO间接反应器储释热循环性能优化

相变悬浮液射流冲击变形状多孔层覆盖壁面的热分析

基于机器学习算法的生物质热解产物产率预测研究

富氧空位锌掺杂PdO/ZrO2催化CO2和苯酚合成碳酸二苯酯