模板沉积法制备大孔高比表面积Fe<sub>3</sub>O<sub>4</sub>/P(GMA-co-EGDMA)磁性复合微球

张宝亮

doi:10.3969/j.issn.0438-1157.2012.04.043

您当前的位置：

首页 >

文章列表页 >

模板沉积法制备大孔高比表面积Fe₃O₄/P(GMA-co-EGDMA)磁性复合微球

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 模板沉积法制备大孔高比表面积Fe₃O₄/P(GMA-co-EGDMA)磁性复合微球
- Preparation of Fe₃O₄/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template
- 化工学报 2012年第4期页码：1308-1314
- 作者机构：
  
  西北工业大学理学院应用化学系,陕西,西安
- 作者简介：
- 基金信息：
- DOI：10.3969/j.issn.0438-1157.2012.04.043
  中图分类号： Q31O611.62
- 网络首发：2012-04-05，
  
  纸质出版：2012-04-05
- 稿件说明：
移动端阅览
张宝亮. 模板沉积法制备大孔高比表面积Fe₃O₄/P(GMA-co-EGDMA)磁性复合微球[J]. 化工学报, 2012,(4):1308-1314. DOI: 10.3969/j.issn.0438-1157.2012.04.043.

张宝亮. Preparation of Fe₃O₄/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template[J]. CIESC Journal, 2012, (4): 1308-1314. DOI: 10.3969/j.issn.0438-1157.2012.04.043.
张宝亮. 模板沉积法制备大孔高比表面积Fe₃O₄/P(GMA-co-EGDMA)磁性复合微球[J]. 化工学报, 2012,(4):1308-1314. DOI: 10.3969/j.issn.0438-1157.2012.04.043. DOI：

张宝亮. Preparation of Fe₃O₄/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template[J]. CIESC Journal, 2012, (4): 1308-1314. DOI: 10.3969/j.issn.0438-1157.2012.04.043. DOI：

摘要

介绍了一种以大孔高比表面积甲基丙烯酸缩水甘油酯（GMA）与二甲基丙烯酸乙二醇酯（EGDMA）共聚交联微球［P(GMA-co-EGDMA)］为模板制备磁性复合微球的简单方法。制备过程包括Fe3+和Fe2+的浸入、OH-作用下孔内铁离子的共沉淀两步。在此过程中考察了浸泡温度、浸泡时间、共沉淀温度以及沉积次数对微球磁含量的影响，确定最佳制备工艺为50℃浸泡4 h，70℃反应1 h，如此反复4次磁含量可以达到45.24%。并通过SEM、VSM、XRD、TGA及压汞仪、激光粒度仪等手段对Fe3O4/P(GMA-co-EGDMA)的形貌、比饱和磁化强度、磁含量及孔性能进行了表征，微球的粒径范围处于100～200 μm之间，平均粒径为162 μm，比饱和磁化强度为10.92 emu·g-1，平均孔径及比表面积分别为60 nm和116 m2·g-1。

Abstract

A simple method for preparation of Fe3O4/P(GMA-co-EGDMA)magnetic composite microspheres using microporous P(GMA-co-EGDMA)microspheres copolymerized with glycidyl methacrylate（GMA)and ethylene glycol dimethacrylate（EGDMA)as template is reported in this paper. The preparation process included soaking of ferrous ion and ferric ion and coprecipitation in the presence of OH-.The influences of soaking temperature

soaking time

coprecipitation temperature and deposition times on magnetic content of magnetic composite microspheres were studied.The optimum preparation process of microporous Fe3O4/P(GMA-co-EGDMA)magnetic composite microspheres was as follows：microporous P(GMA-co-EGDMA)microspheres were soaked at 50℃for 4 h

coprecipitation temperature and time were 70℃ and 1 h respectively.The magnetic content of magnetic composite microspheres was 45.24% when the deposition process was repeated 4 times.The morphology

magnetic properties

magnetic content

pore performance and particle size distribution of Fe3O4/P(GMA-co-EGDMA)were determined by SEM

TGA

XRD

mercury porosimeter and laser particle sizer.It was found that the range of particle size of Fe3O4/P(GMA-co-EGDMA)was 100～200 μm and average particle size was 162 μm

specific saturation magnetization was 10.92 emu·g-1

average pore diameter and specific surface area were 60 nm and 116 m2·g-1 respectively.

关键词

Keywords

references

浏览量

1040

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Fe2+/H2O2体系O2生成路径

Fe2+/Fe3+和Mn2+对低氧曝气过程总氮去除与转化途径的影响

典型陶瓷基体对催化滤芯中催化剂分散及脱硝活性的影响

化学链燃烧中H2S对NiFe2O4氧载体活性的影响机理

O2/H2O燃烧方式下石灰石的间接硫化反应特性

模板沉积法制备大孔高比表面积Fe3O4/P(GMA-co-EGDMA)磁性复合微球

Preparation of Fe3O4/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template

DOI：10.3969/j.issn.0438-1157.2012.04.043

摘要

Abstract

关键词

Keywords

references

模板沉积法制备大孔高比表面积Fe₃O₄/P(GMA-co-EGDMA)磁性复合微球

Preparation of Fe₃O₄/P(GMA-co-EGDMA)magnetic composite microspheres with high specific surface area by deposition of porous template