烧结温度对TiO<sub>2</sub>/不锈钢中空纤维复合膜结构和性能的影响

高佳明; 王明; 马晓华; 许振良

doi:10.11949/j.issn.0438-1157.20180756

您当前的位置：

首页 >

文章列表页 >

烧结温度对TiO₂/不锈钢中空纤维复合膜结构和性能的影响

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 烧结温度对TiO₂/不锈钢中空纤维复合膜结构和性能的影响
- Effect of sintering temperature on structures and properties of TiO₂/stainless steel hollow fiber composite membrane
- 化工学报 2018年第11期页码：4879-4886
- 作者机构：
  
  化学工程联合国家重点实验室, 华东理工大学化学工程研究所膜科学与工程研发中心,上海,200237
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180756
  中图分类号： Q028.8
- 网络首发：2018-11-05，
  
  纸质出版：2018-11-05
- 稿件说明：
移动端阅览
高佳明, 王明, 马晓华, 等. 烧结温度对TiO₂/不锈钢中空纤维复合膜结构和性能的影响[J]. 化工学报, 2018,(11):4879-4886. DOI: 10.11949/j.issn.0438-1157.20180756.

GAO Jiaming, WANG Ming, MA Xiaohua, et al. Effect of sintering temperature on structures and properties of TiO₂/stainless steel hollow fiber composite membrane[J]. CIESC Journal, 2018, (11): 4879-4886. DOI: 10.11949/j.issn.0438-1157.20180756.
高佳明, 王明, 马晓华, 等. 烧结温度对TiO₂/不锈钢中空纤维复合膜结构和性能的影响[J]. 化工学报, 2018,(11):4879-4886. DOI: 10.11949/j.issn.0438-1157.20180756. DOI：

GAO Jiaming, WANG Ming, MA Xiaohua, et al. Effect of sintering temperature on structures and properties of TiO₂/stainless steel hollow fiber composite membrane[J]. CIESC Journal, 2018, (11): 4879-4886. DOI: 10.11949/j.issn.0438-1157.20180756. DOI：

摘要

不锈钢中空纤维膜基膜孔径大，直接涂覆分离层容易产生表面缺陷。在二氧化钛悬浮液中加入聚乙烯醇作为黏结剂，通过真空辅助抽滤法在不锈钢中空纤维基膜表面形成一层均匀的分离层。通过高温烧结得到了TiO2/不锈钢中空纤维复合膜，考察了烧结温度对于TiO2/不锈钢中空纤维复合膜表面分离层形貌和结构的影响。不同烧结温度时，TiO2/不锈钢中空纤维复合膜的表面形貌有所差异；随着烧结温度的升高，不锈钢复合膜的孔径和纯水通量均先升高再下降。当烧结温度为500℃时，表面涂层均匀，孔径分布集中，水通量较高。最后，以SPT-500膜测试了水包油乳液分离效果，分离效率达到99%以上，且具有良好的抗污染性能。

Abstract

Stainless steel hollow fiber membrane has large pore diameter

and the direct coating of the separation layer is liable to cause surface defects. In this paper

polyvinyl alcohol (PVA) is added to the suspension of titanium dioxide as binder

and a uniform separation layer is formed on the surface of stainless steel hollow fiber membrane by vacuum assisted method. TiO2/stainless steel hollow fiber composite membrane was obtained by sintering at high temperature. The influence of sintering temperature on the morphology and structure of the surface separation layer was studied. The surface morphology of TiO2/stainless steel hollow fiber composite membranes was different at different sintering temperatures. The pore size and pure water flux of the composite membranes increased first and then decreased with the increase of sintering temperature. It was found that the surface coating was uniform

the pore size distribution was narrow and the water flux was higher when the sintering temperature was 500℃. Finally

SPT-500 was used to separate oil-water emulsion. The separation efficiency was over 99% and it has a good anti-fouling performance.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

退役光伏组件TPT背板热氧化降解特性研究

用于软包装生物基聚氨酯胶黏剂的制备及耐水热性能研究

从微观尺度揭示木质素热解焦油生成与焦炭结构演化机制

熔融盐辅助生物质热化学高值化转化研究进展

采用高分子非催化还原脱硝的垃圾焚烧工艺伴生固废含氮污染物特征研究

烧结温度对TiO2/不锈钢中空纤维复合膜结构和性能的影响

Effect of sintering temperature on structures and properties of TiO2/stainless steel hollow fiber composite membrane

DOI：10.11949/j.issn.0438-1157.20180756

摘要

Abstract

关键词

Keywords

references

烧结温度对TiO₂/不锈钢中空纤维复合膜结构和性能的影响

Effect of sintering temperature on structures and properties of TiO₂/stainless steel hollow fiber composite membrane