Li3VO4修饰富镍LiNi0.8Co0.1Mn0.1O2正极材料的电化学性能

宋刘斌; 唐福利; 肖忠良

doi:10.11949/j.issn.0438-1157.20180664

您当前的位置：

首页 >

文章列表页 >

Li₃VO₄修饰富镍LiNi_0.8Co_0.1Mn_0.1O₂正极材料的电化学性能

材料化学工程与纳米技术 | 更新时间：2025-12-10

- Li₃VO₄修饰富镍LiNi_0.8Co_0.1Mn_0.1O₂正极材料的电化学性能
- Electrochemical performance of Li₃VO₄ modified Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ cathode materials
- 化工学报 2018年第12期页码：5332-5338
- 作者机构：
  
  长沙理工大学化学与生物工程学院,湖南,长沙,410114
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180664
  中图分类号： M912.9
- 网络首发：2018-12-05，
  
  纸质出版：2018-12-05
- 稿件说明：
移动端阅览
宋刘斌, 唐福利, 肖忠良. Li₃VO₄修饰富镍LiNi_0.8Co_0.1Mn_0.1O₂正极材料的电化学性能[J]. 化工学报, 2018,(12):5332-5338. DOI: 10.11949/j.issn.0438-1157.20180664.

SONG Liubin, TANG Fuli, XIAO Zhongliang. Electrochemical performance of Li₃VO₄ modified Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ cathode materials[J]. CIESC Journal, 2018, (12): 5332-5338. DOI: 10.11949/j.issn.0438-1157.20180664.
宋刘斌, 唐福利, 肖忠良. Li₃VO₄修饰富镍LiNi_0.8Co_0.1Mn_0.1O₂正极材料的电化学性能[J]. 化工学报, 2018,(12):5332-5338. DOI: 10.11949/j.issn.0438-1157.20180664. DOI：

SONG Liubin, TANG Fuli, XIAO Zhongliang. Electrochemical performance of Li₃VO₄ modified Ni-rich LiNi_0.8Co_0.1Mn_0.1O₂ cathode materials[J]. CIESC Journal, 2018, (12): 5332-5338. DOI: 10.11949/j.issn.0438-1157.20180664. DOI：

摘要

采用湿法融合技术及高温固相法合成Li3VO4包覆的LiNi0.8Co0.1Mn0.1O2正极材料。通过X射线衍射（XRD）、扫描电子显微镜（SEM）、透射电子显微镜（TEM）等方法研究材料的结晶相、形貌、微观结构。研究表明，Li3VO4均匀地包覆在LiNi0.8Co0.1Mn0.1O2表面，未改变原材料的材料结构和形貌，包覆层厚度为1～2 nm。不同含量的Li3VO4对LiNi0.8Co0.1Mn0.1O2正极材料进行修饰研究表明，3%（质量）Li3VO4包覆的LiNi0.8Co0.1Mn0.1O2在1 C下100次循环后容量保持率为94.13%，具有最佳的倍率性能和循环性能。此外，循环伏安（CV）和交流阻抗（EIS）分析表明，Li3VO4能提高Li+电导率，抑制活性材料与电解液之间的副反应，提高材料的电化学性能。

Abstract

The Li3VO4 coated LiNi0.8Co0.1Mn0.1O2 cathode material was synthesized by wet fusion technology and high temperature solid phase method. The crystalline phase

morphology and microstructure of materials were studied by X-ray diffraction (XRD)

scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that Li3VO4 is evenly coated on the surface of LiNi0.8Co0.1Mn0.1O2 without changing the material structure and morphology of the raw materials. The coating thickness is 1-2 nm. The modification of LiNi0.8Co0.1Mn0.1O2 cathode material with different content of Li3VO4 shows that 3%(mass) Li3VO4 coated LiNi0.8Co0.1Mn0.1O2 has a capacity retention rate of 94.13% after 100 cycles under 1 C

which has the best multiplier performance and cycling performance. In addition

cyclic voltammetry (CV) and alternating current impedance (EIS) analysis show that Li3VO4 can increase Li+ conductivity

inhibit the side-effect between active material and electrolyte

and improve the electrochemical properties of materials.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

Li2ZrO3包覆LiNi0.8Co0.1Mn0.1O2的复合材料及其电化学性能

正极材料LiNi0.8Co0.1Mn0.1O2的合成工艺优化及电化学性能

共沉淀法制备LiNi1-x-yCoxMnyO2正极材料工艺条件探究

Cr掺杂对富锂锰基正极材料Li1.2Ni0.2Mn0.6O2结构和电化学性能的影响

Li3PO4掺杂的Li(Ni0.5Co0.2Mn0.3)O2锂离子电池正极材料的流变相法合成及电化学性能表征