丙烯酸酯用量对溶胀-嵌段型水性聚氨酯性能的影响

杨东杰; 施一鸣; 单国荣

doi:10.11949/j.issn.0438-1157.20180481

您当前的位置：

首页 >

文章列表页 >

丙烯酸酯用量对溶胀-嵌段型水性聚氨酯性能的影响

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 丙烯酸酯用量对溶胀-嵌段型水性聚氨酯性能的影响
- Effect of acrylate amount on properties of swelling-block waterborne polyurethane
- 化工学报 2018年第11期页码：4856-4861
- 作者机构：
  
  1. 化学工程联合国家重点实验室, 浙江大学化学工程与生物工程学院,浙江,杭州,310027
  2. 杭华油墨股份有限公司,浙江,杭州,310018
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20180481
  中图分类号： Q436.5
- 网络首发：2018-11-05，
  
  纸质出版：2018-11-05
- 稿件说明：
移动端阅览
杨东杰, 施一鸣, 单国荣. 丙烯酸酯用量对溶胀-嵌段型水性聚氨酯性能的影响[J]. 化工学报, 2018,(11):4856-4861.

YANG Dongjie, SHI Yiming, SHAN Guorong. Effect of acrylate amount on properties of swelling-block waterborne polyurethane[J]. CIESC Journal, 2018, (11): 4856-4861.
杨东杰, 施一鸣, 单国荣. 丙烯酸酯用量对溶胀-嵌段型水性聚氨酯性能的影响[J]. 化工学报, 2018,(11):4856-4861. DOI： 10.11949/j.issn.0438-1157.20180481.

YANG Dongjie, SHI Yiming, SHAN Guorong. Effect of acrylate amount on properties of swelling-block waterborne polyurethane[J]. CIESC Journal, 2018, (11): 4856-4861. DOI： 10.11949/j.issn.0438-1157.20180481.

摘要

以甲基丙烯酸甲酯（MMA）、丙烯酸正丁酯（BA）为单体，通过巯基乙醇链转移自由基无规共聚合成端羟基聚丙烯酸酯（PA-OH），采用嵌段共聚法将PA-OH与水性聚氨酯（WPU）嵌段，通过预聚体分散法制得聚丙烯酸酯嵌段水性聚氨酯乳液（WPUA），进而通过乳液聚合法制备了一系列以MMA/BA为单体的聚丙烯酸酯嵌段-溶胀水性聚氨酯复合乳液（WPUA-PA），结果表明WPUA-PA中丙烯酸酯量最多可达到WPUA的240%，当丙烯酸酯量为WPUA的120%时WPUA-PA的性能最佳，此时乳液平均粒径为68 nm、粒径分布指数为0.174，胶膜拉伸强度为13.88 MPa、断裂伸长率为558.3%、吸水率为4.94%，且具有优异的乳液稳定性。

Abstract

Hydroxyl-terminated polyacrylate (PA-OH) was synthesized by free radical copolymerization of methyl methacrylate (MMA) and n-butyl acrylate (BA) using mercaptoethanol as chain transfer. PA-OH was blocked with waterborne polyurethane (WPU) by block polymerization

and then prepared polyacrylate block waterborne polyurethane emulsion (WPUA) by prepolymer dispersion. A series of polyacrylate swelling-block waterborne polyurethane composite emulsions with MMA/BA as the monomer were prepared by emulsion polymerization. The results showed that the dosage of acrylates in WPUA-PA can reach 240% of WPUA. WPUA-PA has the best performance when the dosage of acrylates is 120% of WPUA. The average emulsion particle size is 68 nm

the particle distribution index is 0.174

the tensile strength of the film is 13.88 MPa

the elongation at break is 558.3%

the water absorption is 4.94%

and the emulsion stability is excellent.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

基于GLAE-MLP的炼化装置管道腐蚀健康状态评估方法

GeCl4-MxCly-H2体系下锗-杂质竞争沉积热力学研究

基于机器学习算法的生物质热解产物产率预测研究

部分预混旋流燃烧入口激励下的熵波产生及耗散机制研究

余热梯级驱动热湿调控系统性能影响分析及应用