- 响应曲面法优化氧化铜渣浮选提铜工艺
- Optimization of recycling copper from copper oxide smelting slag by response surface methodology
- 化工学报 2018年第7期页码：3018-3028
- 作者机构：
  
  1. 中国科学院过程工程研究所多相复杂系统国家重点实验室,北京,100190
  2. 2中国科学院大学化学与化工学院,北京,100049
  3. 江西新金叶实业有限公司,江西,上饶,334114
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20171609
  中图分类号： D923
- 网络首发：2018-07-05，
  
  纸质出版：2018-07-05
- 稿件说明：
移动端阅览
王安琪, 王永良, 叶礼平, 等. 响应曲面法优化氧化铜渣浮选提铜工艺[J]. 化工学报, 2018,(7):3018-3028.

WANG Anqi, WANG Yongliang, YE Liping, et al. Optimization of recycling copper from copper oxide smelting slag by response surface methodology[J]. CIESC Journal, 2018, (7): 3018-3028.
王安琪, 王永良, 叶礼平, 等. 响应曲面法优化氧化铜渣浮选提铜工艺[J]. 化工学报, 2018,(7):3018-3028. DOI： 10.11949/j.issn.0438-1157.20171609.

WANG Anqi, WANG Yongliang, YE Liping, et al. Optimization of recycling copper from copper oxide smelting slag by response surface methodology[J]. CIESC Journal, 2018, (7): 3018-3028. DOI： 10.11949/j.issn.0438-1157.20171609.

摘要

江西某炼铜炉渣含铜量高，具有较高的经济价值。由于该铜渣中铜矿物以氧化矿为主，且硫化矿表面被氧化，直接浮选铜回收率低、经济效益差。通过添加活化剂，活化氧化铜矿物，并利用响应曲面中心复合设计原理对浮选工艺条件进行优化，研究氧化钙、硫化钠、Z-200对浮选效果的响应。结果表明，Z-200用量是影响精矿品位和回收率的主要因素，且各响应因素间存在交互效应，在CaO用量为25 g/t，Na2S用量为500 g/t，Z-200用量为100 g/t的最优条件下，闭路试验获得精矿平均品位12%，精矿铜回收率为86.57%，采用该浮选优化工艺能获得较好的回收效果。

Abstract

The copper smelting slag with high copper content from Jiangxi has high economic value. Due to the copper mineral in the copper slag is mainly oxidized ore and the surface of the sulfide ore is oxidized

the copper recovery rate is low and the economic efficiency is poor. In this study

the copper oxide is activated by the addition of activator. To optimize the process conditions

the reaction surface methodology and the center composite design principle are used to investigate the response of the calcium oxide

sodium sulfide and Z-200 collector. The results show that the amount of Z-200 is the main factor affecting the grade and recovery rate of concentrate

and there are interaction effects among the response factors. The flotation index of close circuit test was achieved under the optimum conditions:CaO of 25 g/t

Na2S of 500 g/t and Z-200 of 100 g/t. The average grade of Cu in flotation concentrate is 12%

and the copper recovery is 86.57%

which proved that the flotation optimized process can obtain better recovery effect.

关键词

Keywords

references

浏览量

171

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

响应曲面法优化碳酸锂反应结晶工艺

钛硅分子筛催化α-烯烃环氧化的溶剂效应

氧化-超滤耦合工艺：膜污染控制与新兴污染物降解的进展及挑战

Cu2O晶面在日光下活化过氧乙酸降解水中抗生素的性能及机制

非均相活化过一硫酸盐降解PPCPs：反应机理和分子结构影响研究