纳米CaCO<sub>3</sub>孔径调控及其对碳酸化反应性能的影响

卢尚青; 吴素芳

doi:10.11949/j.issn.0438-1157.20171296

您当前的位置：

首页 >

文章列表页 >

纳米CaCO₃孔径调控及其对碳酸化反应性能的影响

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 纳米CaCO₃孔径调控及其对碳酸化反应性能的影响
- Modulation of nano CaCO₃ pore size and effect on properties of carbonation reaction
- 化工学报 2018年第6期页码：2753-2758
- 作者机构：
  
  浙江大学化学工程与生物工程学院,浙江,杭州,310027
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20171296
  中图分类号： Q116.2
- 网络首发：2018-06-05，
  
  纸质出版：2018-06-05
- 稿件说明：
移动端阅览
卢尚青, 吴素芳. 纳米CaCO₃孔径调控及其对碳酸化反应性能的影响[J]. 化工学报, 2018,(6):2753-2758. DOI: 10.11949/j.issn.0438-1157.20171296.

LU Shangqing, WU Sufang. Modulation of nano CaCO₃ pore size and effect on properties of carbonation reaction[J]. CIESC Journal, 2018, (6): 2753-2758. DOI: 10.11949/j.issn.0438-1157.20171296.
卢尚青, 吴素芳. 纳米CaCO₃孔径调控及其对碳酸化反应性能的影响[J]. 化工学报, 2018,(6):2753-2758. DOI: 10.11949/j.issn.0438-1157.20171296. DOI：

LU Shangqing, WU Sufang. Modulation of nano CaCO₃ pore size and effect on properties of carbonation reaction[J]. CIESC Journal, 2018, (6): 2753-2758. DOI: 10.11949/j.issn.0438-1157.20171296. DOI：

摘要

研究了纳米CaCO3颗粒间孔径调控对CaO与CO2碳酸化反应性能的影响。通过有机模板法制备得到一系列比表面积相近、孔径分布不同的纳米CaCO3，并考察其再生和碳酸化反应性能差异。结果表明：增大平均孔径能促进纳米CaCO3的热分解反应，并降低分解温度约15℃。将平均孔径由15 nm增大至113 nm可显著提高碳酸化反应速率和转化率。研究认为平均孔径和比表面积对碳酸化反应转化率的影响存在交互作用；比表面积小的纳米CaCO3，表现出碳酸化反应转化率受扩散控制影响较大，而比表面积较大的表现为碳酸化反应转化率以表面反应影响控制为主的规律。

Abstract

The pore size modulation of nano CaCO3 particlesand its effect on the CaO carbonation with CO2 have been studied. A series of nano CaCO3 with similar surface area but different pore size distributions were prepared by organic templates

and their differences in regeneration and carbonation properties were tested. The results showed that enlarging the average pore diameter could accelerate the thermal decomposition of CaCO3

and drop the regenerate temperature by 15℃. Analogously

increasing the pore diameter from 15 nm to 113 nm could promote the CaO carbonation rate and conversion. Additionally

researches revealed that the average pore diameter and surface area had a complex affection on CaO carbonation rate and conversion. The carbonation conversion of nano CaCO3 with lower surface area is mostly affected by diffusion

while the conversion of nano CaCO3 with greater surface area is mainly influenced by surface reaction.

关键词

Keywords

references

浏览量

123

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

载体对于胺浸渍类DAC吸附剂性能的影响

有机胺功能化介孔固体吸附剂吸附分离CO2性能研究

三元复合钙基材料CaO-Ca3Al2O6-MgO的合成及其CO2吸附性能

官能团改性铝基MOF的CO2吸附性能及机理研究

富氧空位锌掺杂PdO/ZrO2催化CO2和苯酚合成碳酸二苯酯

纳米CaCO3孔径调控及其对碳酸化反应性能的影响

Modulation of nano CaCO3 pore size and effect on properties of carbonation reaction

DOI：10.11949/j.issn.0438-1157.20171296

摘要

Abstract

关键词

Keywords

references

纳米CaCO₃孔径调控及其对碳酸化反应性能的影响

Modulation of nano CaCO₃ pore size and effect on properties of carbonation reaction