乙烯基对苯二甲酸类甲壳型液晶高分子的形状记忆性能

吴聂; 万里鹰; 李爱妹; 肖春平

doi:10.11949/j.issn.0438-1157.20171089

您当前的位置：

首页 >

文章列表页 >

乙烯基对苯二甲酸类甲壳型液晶高分子的形状记忆性能

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 乙烯基对苯二甲酸类甲壳型液晶高分子的形状记忆性能
- Shape memory properties of mesogen-jacketed liquid crystalline polymers based on vinylterephthalic acid
- 化工学报 2018年第5期页码：2282-2289
- 作者机构：
  
  南昌航空大学材料学院,江西,南昌,330063
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20171089
  中图分类号： Q317
- 网络首发：2018-05-05，
  
  纸质出版：2018-05-05
- 稿件说明：
移动端阅览
吴聂, 万里鹰, 李爱妹, 等. 乙烯基对苯二甲酸类甲壳型液晶高分子的形状记忆性能[J]. 化工学报, 2018,(5):2282-2289.

WU Nie, WAN Liying, LI Aimei, et al. Shape memory properties of mesogen-jacketed liquid crystalline polymers based on vinylterephthalic acid[J]. CIESC Journal, 2018, (5): 2282-2289.
吴聂, 万里鹰, 李爱妹, 等. 乙烯基对苯二甲酸类甲壳型液晶高分子的形状记忆性能[J]. 化工学报, 2018,(5):2282-2289. DOI： 10.11949/j.issn.0438-1157.20171089.

WU Nie, WAN Liying, LI Aimei, et al. Shape memory properties of mesogen-jacketed liquid crystalline polymers based on vinylterephthalic acid[J]. CIESC Journal, 2018, (5): 2282-2289. DOI： 10.11949/j.issn.0438-1157.20171089.

摘要

通过自由基聚合合成了四种基于乙烯基对苯二甲酸类甲壳型液晶高分子（PBPCS，PMPCS，PDCHVT，PbiPCS）。TGA和DMA表征结果表明，这四种甲壳型液晶高分子均具有较好的热稳定性，其侧基末端基团刚性越大，相对应的片材在30～80℃温度区间刚性越大。形状记忆弯角回复测试表明：四种聚合物热压成型的片材都具有很好的形状记忆固定率，均接近100%。形状记忆回复效果与聚合物侧基的末端基团有关，侧基末端基团分别为对丁氧基苯基和环己基（对应聚合物分别为PBPCS和PDCHVT）时，片材显示出较好的形状记忆性能，形状记忆回复率分别为87%和100%。将PDCHVT通过熔融纺丝制成纤维，采用形状记忆循环DMA测试表征其形状记忆性能，结果表明PDCHVT纤维具有稳定的优异的形状记忆性能。

Abstract

Four kinds of mesogen-jacketed liquid crystalline polymers (PBPCS

PMPCS

PDCHVT

PbiPCS) based on vinylterephthalic acid have been synthesized via free radical polymerization. The results of TGA and DMA demonstrate that they all have good thermal stability

and the higher rigidity of the end group

and the greater rigidity of the corresponding polymer sheet in the temperature range of 30-80℃. Through shape memory angle recovery tests

the results indicate that all mesogen-jacketed liquid crystalline polymer sheets have good shape memory fixation ratios close to 100%. The shape memory recovery effect is related to the end group of polymer side chain. When the end groups of side chain are cyclohexyl and P-butoxy phenyl (corresponding polymers are PBPCS and PDCHVT)

the polymer sheets demonstrate good shape memory properties

shape memory recovery ratios are 87% and 100%

respectively. PDCHVT fiber have been prepared by melt spinning

the shape memory properties of PDCHVT fiber have been analyzed by DMA shape memory cycle test

the results show that the fiber exhibits stable and excellent shape memory effect.

关键词

Keywords

references

浏览量

177

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

自由基聚合反应动力学常数测定技术

3D打印微流控通道快速可控制备核壳微纤维

纤维状BPO4/SiO2催化剂的制备及其丙烷氧化脱氢性能

稀土Y2O3基催化涂层对金属纤维表面燃烧器NO排放控制及工程验证

基于递归特性和CNN的上升管内气液两相流型识别研究