不同球径的多孔球层内无机盐溶液过冷度的实验研究

徐笑锋; 章学来; 陈跃; 陈启杨; 李玉洋

doi:10.11949/j.issn.0438-1157.20171063

您当前的位置：

首页 >

文章列表页 >

不同球径的多孔球层内无机盐溶液过冷度的实验研究

流体力学与传递现象 | 更新时间：2025-12-10

- 不同球径的多孔球层内无机盐溶液过冷度的实验研究
- Experimental investigation on inorganic salt solution's supercooling degree under porous spherical layer with different spherical diameters
- 化工学报 2018年第5期页码：1900-1905
- 作者机构：
  
  上海海事大学蓄冷技术研究所,上海,201306
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20171063
  中图分类号： K02
- 网络首发：2018-05-05，
  
  纸质出版：2018-05-05
- 稿件说明：
移动端阅览
徐笑锋, 章学来, 陈跃, 等. 不同球径的多孔球层内无机盐溶液过冷度的实验研究[J]. 化工学报, 2018,(5):1900-1905.

XU Xiaofeng, ZHANG Xuelai, CHEN Yue, et al. Experimental investigation on inorganic salt solution's supercooling degree under porous spherical layer with different spherical diameters[J]. CIESC Journal, 2018, (5): 1900-1905.
徐笑锋, 章学来, 陈跃, 等. 不同球径的多孔球层内无机盐溶液过冷度的实验研究[J]. 化工学报, 2018,(5):1900-1905. DOI： 10.11949/j.issn.0438-1157.20171063.

XU Xiaofeng, ZHANG Xuelai, CHEN Yue, et al. Experimental investigation on inorganic salt solution's supercooling degree under porous spherical layer with different spherical diameters[J]. CIESC Journal, 2018, (5): 1900-1905. DOI： 10.11949/j.issn.0438-1157.20171063.

摘要

无机盐溶液的过冷度极大地影响了相变材料的蓄冷特性。实验以NH4Cl溶液为例，研究了浓度与多孔介质对无机盐溶液的过冷度影响机理。通过改变无机盐溶液浓度与构建多孔介质小球的球径，探究无机盐溶液强化传热传质的方法。实验结果表明：浓度越高，无机盐溶液过冷度越低，离散程度越低，稳定性越高。当浓度达到15%时，溶液平均过冷度较5%浓度溶液可降低17.5%。构建多孔介质小球球径越小，无机盐溶液过冷度越低，离散程度越低，稳定性越高。当球径为5 mm时，溶液平均过冷度较无多孔介质情况下可降低21.7%。

Abstract

The supercooling degree of inorganic salt solution has great effect on the characteristic of the phase change meterials in cool storage. Ammonium chloride solution was chosen as a kind of inorganic salt solution

the experimental system was built to study the influence on supercooling degree of inorganic salt solution under the effection of concentration and porous media. The method of heat transfer enhancement was studied by changing the concentration of inorganic salt solution and the diameter of balls which is constituting the porous media. The experimental results show that with the increase of concentration

the value of inorganic salt solution's supercooling degree and dispersion degree reduced

while the stability increased. Compared with the ammonium chloride solution at the concentration of 5%

the supercooling degree decreased 17.5% when the concentration of chloride solution reached 15%. With the decrease of the diameter of balls which is constituting the porous media

the average value of chloride solution's supercooling degree and dispersion degree decreased

while the stability increased. Compared with the ammonium chloride solution without porous media

the average value of chloride solution's supercooling degree decreased 21.7% when the diameter of balls was 5 mm.

关键词

Keywords

references

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

均匀多孔介质下乙醇溶液的过冷度

不同材料和球径的多孔球层内水的过冷度分析

相变悬浮液射流冲击变形状多孔层覆盖壁面的热分析

长焰煤热解过程中孔的演变及其对挥发分传质影响

固定床反应器中甲醇制芳烃工业催化剂结构影响的研究