多级孔道ZSM-5分子筛超滤膜的制备

姚迅; 彭莉; 徐晓涵; 张春; 顾学红

doi:10.11949/j.issn.0438-1157.20170451

您当前的位置：

首页 >

文章列表页 >

多级孔道ZSM-5分子筛超滤膜的制备

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 多级孔道ZSM-5分子筛超滤膜的制备
- Fabrication of hierarchical ZSM-5 zeolite membranes for ultrafiltration
- 化工学报 2017年第11期页码：4351-4358
- 作者机构：
  
  南京工业大学化工学院, 材料化学工程国家重点实验室, 国家特种分离膜工程技术研究中心,江苏,南京,210009
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170451
  中图分类号： Q028.8
- 网络首发：2017-11-05，
  
  纸质出版：2017-11-05
- 稿件说明：
移动端阅览
姚迅, 彭莉, 徐晓涵, 等. 多级孔道ZSM-5分子筛超滤膜的制备[J]. 化工学报, 2017,(11):4351-4358.

YAO Xun, PENG Li, XU Xiaohan, et al. Fabrication of hierarchical ZSM-5 zeolite membranes for ultrafiltration[J]. CIESC Journal, 2017, (11): 4351-4358.
姚迅, 彭莉, 徐晓涵, 等. 多级孔道ZSM-5分子筛超滤膜的制备[J]. 化工学报, 2017,(11):4351-4358. DOI： 10.11949/j.issn.0438-1157.20170451.

YAO Xun, PENG Li, XU Xiaohan, et al. Fabrication of hierarchical ZSM-5 zeolite membranes for ultrafiltration[J]. CIESC Journal, 2017, (11): 4351-4358. DOI： 10.11949/j.issn.0438-1157.20170451.

摘要

利用二次生长法，以十六烷基三甲基溴化铵（CTAB）为结构导向剂，一步水热合成了多级孔道ZSM-5分子筛膜。结果表明，CTAB球形胶束与分子筛颗粒自组装形成了介孔结构，同时，CTAB胶束及疏水长链抑制了晶体的长大。通过调整CTAB/SiO2摩尔比、合成温度及晶化时间等制膜条件，改变分子筛膜的晶体颗粒尺寸及膜层交联度，实现了分子筛膜介孔结构的有效调节，其孔径范围7~30 nm。在CTAB/SiO2摩尔比为0.05、合成温度180℃、时间20 h下，多级孔分子筛膜纯水渗透通量达到138 kg·m-2·h-1·MPa-1，截留分子量28500，对应平均孔径7.39 nm，达到小孔径超滤的标准。

Abstract

Hierarchical ZSM-5 zeolite membranes were synthesized through secondary growth method in the presence of small amount of cetyltrimethylammonium bromide (CTAB). The results show that CTAB spherical micelles and molecular sieve particles self-assembled to form ordered mesoporous structure. At the same time

the presence of CTAB micelles and hydrophobic long chains suppresses the growth of crystals. By adjusting the CTAB/SiO2 molar ratio

synthesis temperature or crystallization time

the crystal grain size and the crosslinking degree of the zeolite membranes were changed remarkably to realize the simple and effective regulation of the average pore size

ranging from 7 to 30 nm. Under the synthesis at 180℃ for 20 h and the CTAB/SiO2 molar ratio about 0.05

the obtained zeolite membrane exhibited a high water permeability of 138 kg·m-2·h-1·MPa-1

and a molecular weight cut-off(MWCO) of 28500

corresponding to the average pore size of 7.39 nm

achieving the standard of small aperture ultrafiltration.

关键词

Keywords

references

浏览量

253

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

原位合成法制备高通量聚砜超滤膜及其性能研究

基于海水淡化中试的超滤膜清洗工艺及机理

面向健康产业应用需求的膜技术与膜材料

温敏性PVDF/PGS-g-PNIPAM纳米复合超滤膜的制备和性能

多孔陶瓷膜用于碳量子点的分离与纯化