氧化石墨烯改性PVDF超滤膜制备及分离性能

薛娟琴; 王森; 韩小龙; 王玉琪; 李继定

doi:10.11949/j.issn.0438-1157.20170217

您当前的位置：

首页 >

文章列表页 >

氧化石墨烯改性PVDF超滤膜制备及分离性能

分离工程 | 更新时间：2025-12-10

- 氧化石墨烯改性PVDF超滤膜制备及分离性能
- Prepartion and separation performance of GO modified PVDF ultrafiltration membrane
- 化工学报 2017年第9期页码：3466-3473
- 作者机构：
  
  1. 西安建筑科技大学冶金工程学院,陕西,西安,710055
  2. 西北大学化工学院,陕西,西安,710069
  3. 化学工程联合国家重点实验室, 清华大学化学工程系,北京,100084
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170217
  中图分类号： Q028.8
- 网络首发：2017-09-05，
  
  纸质出版：2017-09-05
- 稿件说明：
移动端阅览
薛娟琴, 王森, 韩小龙, 等. 氧化石墨烯改性PVDF超滤膜制备及分离性能[J]. 化工学报, 2017,(9):3466-3473.

XUE Juanqin, WANG Sen, HAN Xiaolong, et al. Prepartion and separation performance of GO modified PVDF ultrafiltration membrane[J]. CIESC Journal, 2017, (9): 3466-3473.
薛娟琴, 王森, 韩小龙, 等. 氧化石墨烯改性PVDF超滤膜制备及分离性能[J]. 化工学报, 2017,(9):3466-3473. DOI： 10.11949/j.issn.0438-1157.20170217.

XUE Juanqin, WANG Sen, HAN Xiaolong, et al. Prepartion and separation performance of GO modified PVDF ultrafiltration membrane[J]. CIESC Journal, 2017, (9): 3466-3473. DOI： 10.11949/j.issn.0438-1157.20170217.

摘要

用N-（三甲氧基硅丙基）乙二胺三乙酸钠（EDTS）对氧化石墨烯进行修饰，制备出亲水的EDTS-GO纳米复合物。然后通过共混的方式将EDTS-GO添加到PVDF中，制备出EDTS-GO改性PVDF超滤膜。接触角分析和红外光谱结果表明，在相转化过程中EDTS-GO转移至膜表面，PVDF膜表面的亲水性增强。系统考察了不同EDTS-GO添加量对膜性能的影响。膜性能测试表明，随着EDTS-GO添加量的增加，PVDF膜的纯水通量先增大然后降低，当添加量为0.5%时，纯水通量达到最大值，711.2 L·（m2·h）-1。此外，抗污染实验表明，EDTS-GO改性的PVDF超滤膜比未改性的PVDF超滤膜具有更强的抗污染性能。

Abstract

EDTS-GO nanocomposites were prepared by decorating graphene oxide (GO) with N-(trimethoxysilylpropyl) ethylenediaminetriacetic acid sodium (EDTS). Then EDTS-GO modified PVDF ultrafiltration membrane was prepared by introducing EDTS-GO through blending method. Contact angle results indicated that the hydrophilicity of PVDF membrane was improved owing to introducing EDTS-GO. This was due to EDTS-GO transferring to membrane surface during phase inversion

which was confirmed by FTIR. The effect of the EDTS-GO addition content on membrane property was investigated systematically. With an increase in EDTS-GO content

the water flux of EDTS-GO modified PVDF membrane initially increased and then decreased and reached to maximum of 711.2 L·(m2·h)-1 in the 0.5% content. Furthermore

antifouling experiment demonstrated EDTS-GO modified PVDF ultrafiltration membrane possessed the stronger fouling-resistant performance than pristine PVDF ultrafiltration membrane.

关键词

Keywords

references

浏览量

382

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

电子效应精准调控的纳米金催化剂在低碳多元醇选择性氧化研究进展

基于机器学习算法的生物质热解产物产率预测研究

烟气脱硫过程含硫量自适应预测与异常状态溯源方法

旋流式冷却造粒塔的优势与风险分析

煤化工废盐中杂质对NaCl和Na2SO4溶剂化影响研究