In625合金和316L不锈钢在NaCl-CaCl<sub>2</sub>-MgCl<sub>2</sub>熔盐中的腐蚀机理

刘波; 魏小兰; 王维龙; 宋明; 丁静

doi:10.11949/j.issn.0438-1157.20170131

您当前的位置：

首页 >

文章列表页 >

In625合金和316L不锈钢在NaCl-CaCl₂-MgCl₂熔盐中的腐蚀机理

表面与界面工程 | 更新时间：2025-12-10

- In625合金和316L不锈钢在NaCl-CaCl₂-MgCl₂熔盐中的腐蚀机理
- Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl₂-MgCl₂ ternary eutectic molten salt
- 化工学报 2017年第8期页码：3202-3210
- 作者机构：
  
  1. 华南理工大学化学与化工学院,广东,广州,510640
  2. 中山大学工学院,广东,广州,510006
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170131
  中图分类号： Q050.9+1
- 网络首发：2017-08-05，
  
  纸质出版：2017-08-05
- 稿件说明：
移动端阅览
刘波, 魏小兰, 王维龙, 等. In625合金和316L不锈钢在NaCl-CaCl₂-MgCl₂熔盐中的腐蚀机理[J]. 化工学报, 2017,(8):3202-3210. DOI: 10.11949/j.issn.0438-1157.20170131.

LIU Bo, WEI Xiaolan, WANG Weilong, et al. Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl₂-MgCl₂ ternary eutectic molten salt[J]. CIESC Journal, 2017, (8): 3202-3210. DOI: 10.11949/j.issn.0438-1157.20170131.
刘波, 魏小兰, 王维龙, 等. In625合金和316L不锈钢在NaCl-CaCl₂-MgCl₂熔盐中的腐蚀机理[J]. 化工学报, 2017,(8):3202-3210. DOI: 10.11949/j.issn.0438-1157.20170131. DOI：

LIU Bo, WEI Xiaolan, WANG Weilong, et al. Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl₂-MgCl₂ ternary eutectic molten salt[J]. CIESC Journal, 2017, (8): 3202-3210. DOI: 10.11949/j.issn.0438-1157.20170131. DOI：

摘要

为了解Cr元素对含铬合金在三元NaCl-CaCl2-MgCl2氯化物熔盐中腐蚀的影响机理，选择两种含铬合金镍基Inconel 625（In625）和铁基奥氏体316L型不锈钢，采用全浸没法分别研究它们在500~700℃下于三元氯化物NaCl-CaCl2-MgCl2低共熔盐中的腐蚀行为，以及接触空气程度与温度对腐蚀的影响。绘制了In625合金和316L不锈钢在熔盐中600℃下浸没21 d的腐蚀速率曲线。采用XRD（X射线衍射仪）、SEM（扫描电镜）和EDX（X射线能谱仪）对In625合金和316L不锈钢的腐蚀产物和截面形貌进行分析。结果表明：两种金属的腐蚀程度随着接触空气的量和腐蚀温度的增加而加大；600℃下腐蚀21 d后金属表面和截面的元素及形貌分析表明，Cr具有优先脱溶性；600℃下腐蚀21 d后在合金截面形成了贫Cr区域；致密的腐蚀层可以降低金属的腐蚀速率；在NaCl-CaCl2-MgCl2三元氯化物熔盐中镍基合金In625拥有比奥氏体不锈钢更好的耐腐蚀性能。

Abstract

Isothermal corrosion of 316L stainless steel and nickel based Inconel 625 alloy was evaluated by total immersion in eutectic NaCl-CaCl2-MgCl2 molten salt at 500-700℃.The effect of chromium (Cr)

air contact

and temperature on corrosion was studied. Corrosion dynamic and velocity curves of 316L and Inconel 625 alloy at 600℃ molten salt for 21 d were obtained. X-Ray diffraction (XRD)

scanning electron microscope (SEM) and X-ray energy spectrometer (EDX) were used to analyze corrosion products and cross section morphologies. The results show that mass loss of the steel and alloy increases with the increase of air contact and corrosion temperature. Element and morphology of metal surface and cross section after 21 d immersion at 600℃ indicate that Cr has a preferential solubility to other elements

which Cr depletion region was observed across cross-section. The dense layer of corrosion products can reduce corrosion rate. Inconel 625 exhibits better corrosion resistance than austenitic stainless steel in NaCl-CaCl2-MgCl2 eutectic molten salt.

关键词

Keywords

references

浏览量

273

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

基于GLAE-MLP的炼化装置管道腐蚀健康状态评估方法

重防腐涂层/TA2在模拟万米超深海环境防护行为的研究

生物基防腐涂层的研究进展

基于实验与有限元的316L不锈钢微动腐蚀损伤与寿命预测研究

发电机定子铜导线腐蚀堵塞机理及控制技术研究进展

In625合金和316L不锈钢在NaCl-CaCl2-MgCl2熔盐中的腐蚀机理

Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl2-MgCl2 ternary eutectic molten salt

DOI：10.11949/j.issn.0438-1157.20170131

摘要

Abstract

关键词

Keywords

references

In625合金和316L不锈钢在NaCl-CaCl₂-MgCl₂熔盐中的腐蚀机理

Corrosion behavior of In625 alloy and 316L stainless steel in NaCl-CaCl₂-MgCl₂ ternary eutectic molten salt