NiO/ZnO-Al₂O₃-SiO₂吸附剂反应吸附脱硫机理

分离工程 | 更新时间：2025-12-10

- NiO/ZnO-Al₂O₃-SiO₂吸附剂反应吸附脱硫机理
- Mechanism of reactive adsorption desulfurization over NiO/ZnO-Al₂O₃-SiO₂ adsorbents
- 化工学报 2017年第8期页码：3089-3099
- 作者机构：
  
  化学工程联合国家重点实验室(华东理工大学),上海,200237
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20170097
  中图分类号： 647.32
- 网络首发：2017-08-05，
  
  纸质出版：2017-08-05
- 稿件说明：
移动端阅览
李凯, 赵基钢, 沈本贤, 等. NiO/ZnO-Al₂O₃-SiO₂吸附剂反应吸附脱硫机理[J]. 化工学报, 2017,(8):3089-3099. DOI: 10.11949/j.issn.0438-1157.20170097.

LI Kai, ZHAO Jigang, SHEN Benxian, et al. Mechanism of reactive adsorption desulfurization over NiO/ZnO-Al₂O₃-SiO₂ adsorbents[J]. CIESC Journal, 2017, (8): 3089-3099. DOI: 10.11949/j.issn.0438-1157.20170097.
李凯, 赵基钢, 沈本贤, 等. NiO/ZnO-Al₂O₃-SiO₂吸附剂反应吸附脱硫机理[J]. 化工学报, 2017,(8):3089-3099. DOI: 10.11949/j.issn.0438-1157.20170097. DOI：

LI Kai, ZHAO Jigang, SHEN Benxian, et al. Mechanism of reactive adsorption desulfurization over NiO/ZnO-Al₂O₃-SiO₂ adsorbents[J]. CIESC Journal, 2017, (8): 3089-3099. DOI: 10.11949/j.issn.0438-1157.20170097. DOI：

摘要

对比考察了N2和H2载气下NiO/ZnO-Al2O3-SiO2吸附剂对模拟汽油的吸附脱硫效果。与H2气氛下的脱硫效果相比，N2载气下吸附剂也具有明显脱硫效果，吸附剂表面积炭导致其脱硫效率降低，从而推断出NiO可以直接进行反应吸附脱硫反应。对不同载气和还原条件下反应前后吸附剂进行XRD、H2-TPR、TOPT和XPS等表征结果表明：反应吸附条件下，吸附剂载体表面NiO难以被还原成单质Ni，说明H2气氛下反应吸附过程中吸附剂中的NiO与单质Ni可能共同参与反应，反应后吸附剂上NiSx存量极少。根据以上研究结果，提出了NiO为活性中心的反应吸附脱硫机理。

Abstract

The reactive adsorption desulfurization (RADS) of a model gasoline was investigated over a NiO/ZnO-Al2O3-SiO2 adsorbent. N2 and H2 were used as carrier gases

and their desulfurization results were compared. Results showed that the adsorbent performed well when using N2 as the carrier gas. Carbon deposition on the surface is the main reason of the drop of desulfurization efficiency. This indicates that NiO could directly react with sulfur compounds in gasoline without the presence of H2. Results of XRD

H2-TPR

TOPT and XPS showed that NiO is hard to be reduced under conditions of RADS. RADS process mainly depends on the reaction of NiO and Ni to remove sulfur compounds. At last

a possible RADS mechanism was presented and discussed.

关键词

Keywords

references

浏览量

273

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

过渡金属基氮掺杂炭的构筑及其脱硫性能研究

中间体自由基断裂对丙烯酸甲酯/甲基丙烯酸甲酯RAFT聚合的影响

富酸位13X分子筛的制备及其超深度吸附脱除生物柴油中硫醇

兼具加氢和脱硫活性的富含Niδ+非晶态NiP@γ-Al2O3催化剂的构筑及其用于石油树脂加氢的性能研究

电化学脱盐机理及相关研究进展