MoO<sub>3</sub>/石墨烯/碳纳米管复合阴极在MFCs中的应用

郭文显; 陈妹琼; 程发良

doi:10.11949/j.issn.0438-1157.20161195

您当前的位置：

首页 >

文章列表页 >

MoO₃/石墨烯/碳纳米管复合阴极在MFCs中的应用

能源和环境工程 | 更新时间：2025-12-10

- MoO₃/石墨烯/碳纳米管复合阴极在MFCs中的应用
- Application of MoO₃/graphene/carbon nano-tube composite cathode for MFCs
- 化工学报 2017年第3期
- 作者机构：
  
  1. 东莞理工学院城市学院, 东莞市绿色能源重点实验室,广东,东莞,523419
  2. 东莞理工学院, 广东省新型纳米材料工程技术研究中心,广东,东莞,523808
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20161195
  中图分类号： 646X382X703
- 网络首发：2017-03-05，
  
  纸质出版：2017-03-05
- 稿件说明：
移动端阅览
郭文显, 陈妹琼, 程发良. MoO₃/石墨烯/碳纳米管复合阴极在MFCs中的应用[J]. 化工学报, 2017,(3). DOI: 10.11949/j.issn.0438-1157.20161195.

GUO Wenxian, CHEN Meiqiong, CHENG Faliang. Application of MoO₃/graphene/carbon nano-tube composite cathode for MFCs[J]. CIESC Journal, 2017, (3). DOI: 10.11949/j.issn.0438-1157.20161195.
郭文显, 陈妹琼, 程发良. MoO₃/石墨烯/碳纳米管复合阴极在MFCs中的应用[J]. 化工学报, 2017,(3). DOI: 10.11949/j.issn.0438-1157.20161195. DOI：

GUO Wenxian, CHEN Meiqiong, CHENG Faliang. Application of MoO₃/graphene/carbon nano-tube composite cathode for MFCs[J]. CIESC Journal, 2017, (3). DOI: 10.11949/j.issn.0438-1157.20161195. DOI：

摘要

采用简单的水热合成法制备了氧化钼（MoO3）/石墨烯（GNS）/碳纳米管（CNT）复合材料。用扫描电子显微镜（SEM）和X射线衍射仪（XRD）表征了材料的形貌和结构。用循环伏安（CV）和线性扫描（LSV）测试了材料的氧还原催化性能，结果发现，复合材料的氧还原电流和起始电位均大大优于单一的MoO3，表现出较好的催化性能。含有3 mg·cm-2 MoO3/GNS/CNT复合材料作为阴极催化剂的MFC最大功率密度为510 mW·m-2，达到商业铂碳的83%。因此，廉价的MoO3/GNS/CNT复合材料作为MFC阴极氧还原催化剂具有巨大的应用潜力。

Abstract

The MoO3/graphene/carbon nano-tube composites were synthesized via a facile hydrothermal method. The morphology of the materials were observed using scanning electron microscope (SEM) and the structures were characterized

with X-ray diffraction (XRD). The electro catalytic activity of oxygen reduction of the materials were measured by cyclic voltammetry (CV) and linear sweep voltammetry (LSV). The results revealed that the composites exhibited better electro catalytic activity towards oxygen reduction with a higher oxygen reduction current and more positive oneset potential than pure MoO3. The microbial fuel cell assembled with 3 mg·cm-2 MoO3/GNS/CNT composites as cathode catalyst delivered a higher power density of 510 mW·m-2

which was 83% as much as the MFCs using Pt/C-catalyst cathode. Therefore

the inexpensive MoO3/GNS/CNT composites as MFCs cathode oxygen reduction catalyst had great potential for application.

关键词

Keywords

references

浏览量

680

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

厌氧流化床微生物燃料电池空气阴极研究

合金催化剂在电化学合成氨中的应用研究

直接Z型异质结体系光催化还原二氧化碳研究进展

仿生材料的构建及其在水环境化学领域中的研究进展

ZIF-67衍生Co/NC多孔碳材料的改性及其电催化水氧化性能

MoO3/石墨烯/碳纳米管复合阴极在MFCs中的应用

Application of MoO3/graphene/carbon nano-tube composite cathode for MFCs

DOI：10.11949/j.issn.0438-1157.20161195

摘要

Abstract

关键词

Keywords

references

MoO₃/石墨烯/碳纳米管复合阴极在MFCs中的应用

Application of MoO₃/graphene/carbon nano-tube composite cathode for MFCs