添加纳米SiO<sub>2</sub>对四元溴化盐相变热物性的影响

熊亚选; 栗博; 吴玉庭; 史建峰; 马重芳

doi:10.11949/j.issn.0438-1157.20161015

您当前的位置：

首页 >

文章列表页 >

添加纳米SiO₂对四元溴化盐相变热物性的影响

热力学 | 更新时间：2025-12-10

- 添加纳米SiO₂对四元溴化盐相变热物性的影响
- Improving phase change thermal properties of quaternary bromides by adding SiO₂ nanoparticle
- 化工学报 2017年第4期页码：1299-1305
- 作者机构：
  
  1. 北京建筑大学供热供燃气通风及空调工程北京市重点实验室,北京,100044
  2. 北京工业大学传热强化与过程节能教育部重点实验室暨传热与能源利用北京市重点实验室,北京,100124
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20161015
  中图分类号： B321
- 网络首发：2017-04-05，
  
  纸质出版：2017-04-05
- 稿件说明：
移动端阅览
熊亚选, 栗博, 吴玉庭, 等. 添加纳米SiO₂对四元溴化盐相变热物性的影响[J]. 化工学报, 2017,(4):1299-1305. DOI: 10.11949/j.issn.0438-1157.20161015.

XIONG Yaxuan, LI Bo, WU Yuting, et al. Improving phase change thermal properties of quaternary bromides by adding SiO₂ nanoparticle[J]. CIESC Journal, 2017, (4): 1299-1305. DOI: 10.11949/j.issn.0438-1157.20161015.
熊亚选, 栗博, 吴玉庭, 等. 添加纳米SiO₂对四元溴化盐相变热物性的影响[J]. 化工学报, 2017,(4):1299-1305. DOI: 10.11949/j.issn.0438-1157.20161015. DOI：

XIONG Yaxuan, LI Bo, WU Yuting, et al. Improving phase change thermal properties of quaternary bromides by adding SiO₂ nanoparticle[J]. CIESC Journal, 2017, (4): 1299-1305. DOI: 10.11949/j.issn.0438-1157.20161015. DOI：

摘要

熔点、熔化潜热和分解温度是熔盐传热蓄热材料的重要热物性参数。以分析纯NaBr、KBr、CaBr2和LiBr配制四元溴化盐，分别将颗粒平均直径为10、20、50 nm的纳米SiO2颗粒按一定含量分散入所配制四元溴化盐中配制得到25种不同含量和粒径的纳米SiO2溴化盐，利用DSC法研究添加纳米SiO2含量和粒径对四元溴化盐熔点、熔化潜热及分解温度的影响。结果表明，随着纳米SiO2含量的增大，溴化盐的熔点先降低后升高，但变化范围较小；熔化潜热先升高后逐步降低，变化较大。添加10 nm SiO2颗粒含量为质量分数1.5%时，最大熔化潜热为47.06 J·g-1，提高89.6%；添加10 nm SiO2颗粒含量为质量分数0.7%时，最高分解温度为876.3℃。

Abstract

Melt temperature

fusion heat and decomposition temperature are three fundamental thermo-physical properties of molten salt. Based on NaBr (AR)

KBr (AR)

CaBr2 (AR) and LiBr (AR) 25 quaternary bromides with different average diameter (10 nm

20 nm and 50 nm) and mass concentration of SiO2 nanoparticles were prepared. Differential scanning calorimetry (DSC) was employed to investigate melt temperature

fusion heat and decomposition temperature of the 25 quaternary bromides with SiO2 nanoparticles. Experimental results showed that the melting point of the nano-quaternary bromides decreased first and then increased subsequently with the increase of SiO2 nanoparticles. The fusion heat increased first and then decreased

which varies greatly with the increase of SiO2 nanoparticles. As the mass concentration of the 10 nm SiO2 nanoparticles is 1.5%

nano-quaternary bromides reached a maximum fusion heat of 47.06 J·g-1

which increased by 89.6%. As the mass concentration of the 10 nm SiO2 nanoparticles is 0.7%

nano-quaternary bromides reached a maximum decomposition temperature of 876.3℃.

关键词

Keywords

references

浏览量

230

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

碳酸盐复合蓄热材料的制备及热物性研究

静电场作用下液体凝固点变化的热力学机理

太阳能直接吸收相变集-蓄热器的放热特性研究

基于电池冷却用新型脉动热管性能的实验研究

污泥焚烧炉渣基定型复合相变储热材料的制备和性能

添加纳米SiO2对四元溴化盐相变热物性的影响

Improving phase change thermal properties of quaternary bromides by adding SiO2 nanoparticle

DOI：10.11949/j.issn.0438-1157.20161015

摘要

Abstract

关键词

Keywords

references

添加纳米SiO₂对四元溴化盐相变热物性的影响

Improving phase change thermal properties of quaternary bromides by adding SiO₂ nanoparticle