SiO<sub>2</sub>表面原位接枝聚环氧丙烷高分子刷的制备及表征

曹芬; 陈可平; 田春蓉; 林晓艳; 梁书恩; 贾晓蓉; 王建华

doi:10.11949/j.issn.0438-1157.20160831

您当前的位置：

首页 >

文章列表页 >

SiO₂表面原位接枝聚环氧丙烷高分子刷的制备及表征

材料化学工程与纳米技术 | 更新时间：2025-11-26

- SiO₂表面原位接枝聚环氧丙烷高分子刷的制备及表征
- Preparation and characterization of polypropylene oxide polymer brushes grafted SiO₂ by in-situ polymerization
- 化工学报 2017年第1期页码：430-436
- 作者机构：
  
  1. 西南科技大学材料科学与工程学院,四川,绵阳,621010
  2. 中国工程物理研究院化工材料研究所,四川,绵阳,621900
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160831
  中图分类号： 633.1
- 网络首发：2017-01-05，
  
  纸质出版：2017-01-05
- 稿件说明：
移动端阅览
曹芬, 陈可平, 田春蓉, 等. SiO₂表面原位接枝聚环氧丙烷高分子刷的制备及表征[J]. 化工学报, 2017,(1):430-436. DOI: 10.11949/j.issn.0438-1157.20160831.

CAO Fen, CHEN Keping, TIAN Chunrong, et al. Preparation and characterization of polypropylene oxide polymer brushes grafted SiO₂ by in-situ polymerization[J]. CIESC Journal, 2017, (1): 430-436. DOI: 10.11949/j.issn.0438-1157.20160831.
曹芬, 陈可平, 田春蓉, 等. SiO₂表面原位接枝聚环氧丙烷高分子刷的制备及表征[J]. 化工学报, 2017,(1):430-436. DOI: 10.11949/j.issn.0438-1157.20160831. DOI：

CAO Fen, CHEN Keping, TIAN Chunrong, et al. Preparation and characterization of polypropylene oxide polymer brushes grafted SiO₂ by in-situ polymerization[J]. CIESC Journal, 2017, (1): 430-436. DOI: 10.11949/j.issn.0438-1157.20160831. DOI：

摘要

通过“Stober”法制备出单分散球形SiO2粒子，并采用3-缩水甘油醚氧基丙基三甲氧基硅烷对其表面进行功能化修饰，然后，利用异丙醇铝作为多相催化剂，原位引发环氧丙烷（PO）单体开环聚合，制得了聚环氧丙烷（PPO）高分子刷接枝改性的SiO2（PPO-g-SiO2）。研究了单体添加量、反应温度及反应时间等因素对聚环氧丙烷高分子刷接枝量的影响规律。采用红外光谱（FT-IR）、X射线光电子能谱（XPS）、透射电子显微镜（TEM）、扫描电子显微镜（SEM）及热重分析（TGA）等分析方法对制备的PPO-g-SiO2的化学结构、微观形貌以及接枝量进行了表征。结果显示，当单体添加量为2.38 mol·L-1，反应温度为80℃，反应时间为24 h时，PPO在SiO2表面的接枝量可达23.56%（质量分数）；其厚度约为15 nm。

Abstract

Monodispersed spherical SiO2 particles were successfully prepared by Stober method

and the functional modification of SiO2 was obtained by the reaction of Si-OH with 3-glycidoxypropyltrimethoxysilane(GPS).By using aluminum isopropoxide as a heterogeneous catalyst to initiate in-situ ring-opening polymerization of the propylene oxide(PO) monomers

a polypropylene oxide(PPO) polymer brush grafted SiO2(PPO-g-SiO2) was obtained.The effects of the amount of monomer

reaction temperature and reaction time on the grafted polymer brushes were discussed.In addition

the chemical structure and morphology of PPO-g-SiO2 and grafted amount were characterized by Fourier transform infrared spectroscopy(FT-IR)

X-ray photoelectron spectroscopy(XPS)

transmission electron microscopy(TEM)

scanning electron microscope(SEM) and thermogravimetric analysis(TGA).The results show when the amount of the monomer addition is 2.38 mol·L-1

reaction temperature is 80℃

and reaction time is 24 h

respectively

the PPO graft quantity is up to 23.56%(mass) on SiO2 surface and the thickness is about 15 nm.

关键词

Keywords

references

浏览量

261

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

钠基干法脱硫灰协同飞灰脱钙工艺路径研究

强基材附着力水下超疏油涂层的设计和防污性能研究

蒸氨时间对Cu/SiO2催化草酸二甲酯加氢制乙二醇反应性能的影响

煤气化熔渣结构的多尺度研究进展

NKC-9催化环硅氧烷开环聚合动力学及其建模研究

SiO2表面原位接枝聚环氧丙烷高分子刷的制备及表征

Preparation and characterization of polypropylene oxide polymer brushes grafted SiO2 by in-situ polymerization

DOI：10.11949/j.issn.0438-1157.20160831

摘要

Abstract

关键词

Keywords

references

SiO₂表面原位接枝聚环氧丙烷高分子刷的制备及表征

Preparation and characterization of polypropylene oxide polymer brushes grafted SiO₂ by in-situ polymerization