- Effect of composition and structure of macromolecular polyurethane surfactant on structures and properties of waterborne polyurethane-acrylate latex
- 化工学报 2016年第12期页码：5208-5214
- 作者机构：
  
  1. 合肥工业大学化学与化工学院,安徽,合肥,230009
  2. 安徽省先进功能材料与器件重点实验室,安徽,合肥,230009
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160794
  中图分类号： Q323.8
- 网络首发：2016-12-05，
  
  纸质出版：2016-12-05
- 稿件说明：
移动端阅览
王海利, 范仁祥, 方华高, 等. 聚氨酯大分子表面活性剂组成结构对WPUA胶粒结构及其膜性能的影响[J]. 化工学报, 2016,(12):5208-5214.

WANG Haili, FAN Renxiang, FANG Huagao, et al. Effect of composition and structure of macromolecular polyurethane surfactant on structures and properties of waterborne polyurethane-acrylate latex[J]. CIESC Journal, 2016, (12): 5208-5214.
王海利, 范仁祥, 方华高, 等. 聚氨酯大分子表面活性剂组成结构对WPUA胶粒结构及其膜性能的影响[J]. 化工学报, 2016,(12):5208-5214. DOI： 10.11949/j.issn.0438-1157.20160794.

WANG Haili, FAN Renxiang, FANG Huagao, et al. Effect of composition and structure of macromolecular polyurethane surfactant on structures and properties of waterborne polyurethane-acrylate latex[J]. CIESC Journal, 2016, (12): 5208-5214. DOI： 10.11949/j.issn.0438-1157.20160794.

摘要

设计了聚合度相同，但组成结构不同的聚氨酯大分子表面活性剂（PUS），并将此大分子表面活性剂用于甲基丙烯酸甲酯（MMA）的聚合，制备出乳胶粒结构不同的水性聚氨酯-丙烯酸酯乳液（WPUA），乳液经干燥成膜后得到不同的样膜。应用透射电镜（TEM）、Zeta纳米粒度仪及旋转黏度计对WPUA乳胶粒形貌、粒径和乳液黏度进行了测试与表征，通过ATR-FTIR、吸水率测试、万能材料试验机和紫外-可见光谱仪对WPUA膜的结构、耐水性、力学性能和物理老化行为进行了研究。结果表明，PUS组成结构会影响WPUA乳胶粒的结构，进而影响形成的WPUA膜的性能。WPUA-PCDL乳胶粒的核壳结构明显，其膜的力学和耐老化性能较好。

Abstract

Macromolecular polyurethane surfactants(PUS) with equal degree of polymerization but different compositions and structures were designed and synthesized by reacting PCDL

PBA and PPG with isophorone diisocyanate(IPDI). Methyl methacrylate(MMA) monomer was polymerized in PUS micelles to prepare WPUA emulsions and dried latex films with different latex structure and morphology. Transmission electron microscopy(TEM)

Zeta nanosizer

and rotating viscometer were employed to characterize latex morphology

particle size

and shear viscosity of WPUA emulsions. ATR-FTIR

water absorption measurement

electromechanical universal testing machine

and UV-Vis spectroscopy were employed to characterize structures

water resistance

mechanical properties

and physical aging behaviors of WPUA films. PUS composition and structure had a significant influence on morphology and structure of WPUA latexes and properties of dried films. Distinct core-shell structure was achieved in WPUA latex using PCDL-based PUS as macromolecular surfactant. WPUA-PCDL film exhibited good mechanical and aging-resistant properties.

关键词

Keywords

references

浏览量

295

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

水性环氧丙烯酸酯乳液涂层成膜性能

石蜡/水相变乳液的制备与性能

阴/阳离子Gemini表面活性剂复配体系的泡沫稳定性调控及构效关系研究

基于改性PVDF膜的新风全热回收特性研究

季铵盐氟碳表面活性剂复配体系的性能研究