活性炭纤维负载Pr3+:Y2SiO5/TiO2复合材料的制备与性能

徐萌川; 王亚淼; 杨毅; 焦岩; 刘颖; 颜学武

doi:10.11949/j.issn.0438-1157.20160716

您当前的位置：

首页 >

文章列表页 >

活性炭纤维负载Pr³⁺:Y₂SiO₅/TiO₂复合材料的制备与性能

材料化学工程与纳米技术 | 更新时间：2025-12-10

- 活性炭纤维负载Pr³⁺:Y₂SiO₅/TiO₂复合材料的制备与性能
- Preparation and performance of Pr³⁺: Y₂SiO₅/TiO₂ composites deposited on activated carbon fiber
- 化工学报 2016年第11期页码：4885-4891
- 作者机构：
  
  1. 南京理工大学环境与生物工程学院,江苏,南京,210094
  2. 南京信息工程大学环境科学与工程学院, 江苏省环境净化材料工程技术研究中心,江苏,南京,210044
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160716
  中图分类号： 788
- 网络首发：2016-11-05，
  
  纸质出版：2016-11-05
- 稿件说明：
移动端阅览
徐萌川, 王亚淼, 杨毅, 等. 活性炭纤维负载Pr³⁺:Y₂SiO₅/TiO₂复合材料的制备与性能[J]. 化工学报, 2016,(11):4885-4891. DOI: 10.11949/j.issn.0438-1157.20160716.

XU Mengchuan, WANG Yamiao, YANG Yi, et al. Preparation and performance of Pr³⁺: Y₂SiO₅/TiO₂ composites deposited on activated carbon fiber[J]. CIESC Journal, 2016, (11): 4885-4891. DOI: 10.11949/j.issn.0438-1157.20160716.
徐萌川, 王亚淼, 杨毅, 等. 活性炭纤维负载Pr³⁺:Y₂SiO₅/TiO₂复合材料的制备与性能[J]. 化工学报, 2016,(11):4885-4891. DOI: 10.11949/j.issn.0438-1157.20160716. DOI：

XU Mengchuan, WANG Yamiao, YANG Yi, et al. Preparation and performance of Pr³⁺: Y₂SiO₅/TiO₂ composites deposited on activated carbon fiber[J]. CIESC Journal, 2016, (11): 4885-4891. DOI: 10.11949/j.issn.0438-1157.20160716. DOI：

摘要

为了提高纳米TiO2对太阳光的利用率和实现光催化剂的回收再利用，采用溶胶-凝胶法将上转换荧光材料与纳米TiO2复合，通过负载于活性炭纤维（ACF）表面制备了Pr3+：Y2SiO5/TiO2/ACF复合材料。运用XRD、FT-IR、SEM、FS、UV-vis DRS等对材料的结构及性能进行了综合表征，并以亚甲基蓝为模拟污染物评价复合材料的可见光催化活性，考察了材料制备过程中煅烧温度、负载次数等制备条件对复合材料可见光下催化性能的影响。结果表明，在浸渍2次、800℃煅烧的制备条件下，复合材料中TiO2为锐钛矿相（占34.1%）与金红石相（占65.9%）的混合相，亚甲基蓝（15 mg·L-1）12 h内去除率高达93.8%，反应符合拟一级动力学，反应速率常数为0.2471 h-1，回收再生利用4次后去除率仍保持在75%以上。

Abstract

In order to improve sunlight utilization as well as to recycle and reuse photocatalyst of titanium dioxide

Pr3+:Y2SiO5/TiO2/ACF composites were prepared by sol-gel technique of anchoring upconversion fluorescent material and nano-titanium dioxide on activated carbon fiber (ACF). Structures and properties of the Pr3+:Y2SiO5/TiO2/ACF composites were characterized by XRD

FT-IR

SEM

and UV-vis DRS. Photocatalytic activity of the composites in the visible light region was evaluated with methylene blue solution as model pollutant and studied the effect of fabrication conditions such as calcination temperature and number of coating layers. The experimental results showed that TiO2 in Pr3+:Y2SiO5/TiO2/ACF composite contained both anatase (34.1%) and rutile (65.9%) when prepared by double coating and 800℃ calcination. This composite had the highest visible-light photocatalytic activity which degraded methylene blue (15 mg·L-1) high as 93.8% in 12 h. The photodegradation followed pseudo first order kinetics with reaction rate constant is 0.2471 h-1. Pr3+:Y2SiO5/TiO2/ACF composite remained degradation rate above 75% after recycled and regenerated for use four times.

关键词

Keywords

references

浏览量

180

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

γ辐照作用下GFRP热分解动力学研究

C/TiO2-SO42-的制备及其光解水性能

化学链燃烧中H2S对NiFe2O4氧载体活性的影响机理

介孔Cr(OH)3的制备及其对钒(Ⅴ)离子的吸附性能

H2O2预氧化对BFA复合融雪剂性能的影响及其融雪机理