GO/PEDOT复合材料修饰阳极的制备及其在MFC中的应用

霍庆城; 黄仁亮; 齐崴; 苏荣欣; 何志敏

doi:10.11949/j.issn.0438-1157.20160595

您当前的位置：

首页 >

文章列表页 >

GO/PEDOT复合材料修饰阳极的制备及其在MFC中的应用

能源和环境工程 | 更新时间：2025-11-26

- GO/PEDOT复合材料修饰阳极的制备及其在MFC中的应用
- Preparation and application of GO/PEDOT composite anode for MFC
- 化工学报 2016年67卷第10期页码：4406-4412
- 作者机构：
  
  1. 天津大学化工学院, 化学工程研究所,天津,300072
  2. 天津大学环境科学与工程学院,天津,300072
  3. 化学工程联合国家重点实验室(天津大学),天津,300072
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160595
  中图分类号： 646X382
- 网络首发：2016-10-05，
  
  纸质出版：2016-10-05
- 稿件说明：
移动端阅览
霍庆城, 黄仁亮, 齐崴, 等. GO/PEDOT复合材料修饰阳极的制备及其在MFC中的应用[J]. 化工学报, 2016,67(10):4406-4412.

HUO Qingcheng, HUANG Renliang, QI Wei, et al. Preparation and application of GO/PEDOT composite anode for MFC[J]. CIESC Journal, 2016, 67(10): 4406-4412.
霍庆城, 黄仁亮, 齐崴, 等. GO/PEDOT复合材料修饰阳极的制备及其在MFC中的应用[J]. 化工学报, 2016,67(10):4406-4412. DOI： 10.11949/j.issn.0438-1157.20160595.

HUO Qingcheng, HUANG Renliang, QI Wei, et al. Preparation and application of GO/PEDOT composite anode for MFC[J]. CIESC Journal, 2016, 67(10): 4406-4412. DOI： 10.11949/j.issn.0438-1157.20160595.

摘要

微生物燃料电池（MFC）是一种利用微生物将有机物中的化学能直接转化成电能的装置，通过改善阳极特性可以有效提高微生物燃料电池的产电性能。通过恒电流法电沉积制备了氧化石墨烯/聚3

4-乙烯二氧噻吩（GO/PEDOT）复合材料修饰碳毡（CF）阳极。通过循环伏安法和交流阻抗法考察了电极特性。将其应用到微生物燃料电池中，对其产电性能进行评价。结果表明，GO/PEDOT-CF电极具有较大的比表面积和优良的电化学性能；以GO/PEDOT-CF为阳极的微生物燃料电池，产电性能良好，其最大功率密度和最大电流密度达到1.138 W·m-2和4.714 A·m-2，分别是未修饰阳极的4.80倍和5.51倍。因此，GO/PEDOT复合材料是一种优良的阳极修饰材料，可有效提高MFC的产电性能。

Abstract

A microbial fuel cell (MFC) is an innovative power output device. The properties of the anode is a critical factor for improving the performance of MFC. In this study

a graphene oxide/poly(3

4-ethylenedioxythiophene) (GO/PEDOT) composite was prepared and used for modification of carbon felt (CF) via the electrodeposition with constant current. The cyclic voltammetry and electrochemical impedance characteristics of the electrode were evaluated. Furthermore

the as-prepared anode was applied in MFC and its electrogenesis capacity was investigated. The results showed that the GO/PEDOT-CF electrode had a large specific surface area and good electrochemical performance. When the GO/PEDOT-CF anode was used in MFC

the maximum power density and current density were up to 1.138 W·m-2 and 4.714 A·m-2

respectively

which were 4.80 times and 5.51 times higher than those of unmodified anodes. These results demonstrated that the GO/PEDOT composite is a kind of effective anode materials for improving electricity generation of MFC.

关键词

Keywords

references

浏览量

379

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

基于金纳米颗粒修饰二氧化硅纳米花的生物传感器构建及应用

木质素衍生炭在碱金属离子电池负极中的研究进展

具有优异锂存储性能的蛋黄蛋壳结构FeS2@CFs薄膜电极

热电池电解质与隔膜材料研究进展

核壳结构米粒状FeS2/C纳米材料制备及储锂性能研究