WC/TiO<sub>2</sub>纳米复合材料晶相形成机理及电催化性能

王晓娟; 毛信表; 李国华; 马淳安

doi:10.11949/j.issn.0438-1157.20160531

您当前的位置：

首页 >

文章列表页 >

WC/TiO₂纳米复合材料晶相形成机理及电催化性能

材料化学工程与纳米技术 | 更新时间：2025-12-10

- WC/TiO₂纳米复合材料晶相形成机理及电催化性能
- Crystal phase formation mechanism and electrocatalytical properties of WC/TiO₂ nanocomposites
- 化工学报 2016年第11期页码：4873-4877
- 作者机构：
  
  1. 宁波检验检疫科学技术研究院,浙江,宁波,315012
  2. 浙江工业大学化学工程与材料学院, 绿色化学合成技术国家重点实验室培育基地,浙江,杭州,310032
  3. 宁波出入境检验检疫局,浙江,宁波,315012
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160531
  中图分类号： 646
- 网络首发：2016-11-05，
  
  纸质出版：2016-11-05
- 稿件说明：
移动端阅览
王晓娟, 毛信表, 李国华, 等. WC/TiO₂纳米复合材料晶相形成机理及电催化性能[J]. 化工学报, 2016,(11):4873-4877. DOI: 10.11949/j.issn.0438-1157.20160531.

WANG Xiaojuan, MAO Xinbiao, LI Guohua, et al. Crystal phase formation mechanism and electrocatalytical properties of WC/TiO₂ nanocomposites[J]. CIESC Journal, 2016, (11): 4873-4877. DOI: 10.11949/j.issn.0438-1157.20160531.
王晓娟, 毛信表, 李国华, 等. WC/TiO₂纳米复合材料晶相形成机理及电催化性能[J]. 化工学报, 2016,(11):4873-4877. DOI: 10.11949/j.issn.0438-1157.20160531. DOI：

WANG Xiaojuan, MAO Xinbiao, LI Guohua, et al. Crystal phase formation mechanism and electrocatalytical properties of WC/TiO₂ nanocomposites[J]. CIESC Journal, 2016, (11): 4873-4877. DOI: 10.11949/j.issn.0438-1157.20160531. DOI：

摘要

以金红石相纳米TiO2为载体，偏钨酸铵为钨源，采用表面修饰技术制备了纳米复合材料的前体，将前体在甲烷/氢气气氛下还原碳化并采用XRD对其进行表征，研究了还原碳化温度、时间对纳米复合材料晶相组成的影响，并探讨了WC/TiO2纳米复合材料的形成机理。通过扫描电子显微镜、热重-差热分析等手段对WC/TiO2纳米复合材料的形态结构和热稳定性进行了表征。采用循环伏安法研究了纳米复合材料物相组成与电催化性能之间的关系，结果表明由WC和TiO2两相组成的WC/TiO2纳米复合材料对对硝基苯酚电还原反应的电催化性能最佳。

Abstract

Tungsten carbide and titania (WC/TiO2) nanocomposites were fabricated by surface modification of rutile titania reacting with ammonium metatungstate and followed by in situ reduction and carburization of the modified rutile in CH4/H2 atmosphere. The influence of temperature and time of in situ reduction and carburization on phase structures of WC/TiO2 nanocomposites were investigated by XRD characterization on nanocomposites

and the formation mechanism of crystal phases in WC/TiO2 nanocomposites was discussed. The morphology and thermal stability of WC/TiO2 nanocomposites were studied by SEM and TG-DTA

respectively. Electrocatalytical properties of the WC/TiO2 nanocomposites with different phase structures were investigated by cyclic voltammetry. Results showed that WC/TiO2 nanocomposites composed of both WC and TiO2 crystal phase exhibited the best catalytic activity for p-nitrophenol (PNP) electroreduction.

关键词

Keywords

references

浏览量

126

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

木质素衍生炭在碱金属离子电池负极中的研究进展

Pt/WC-CNTs催化剂的制备及其对氧还原的电催化性能

隔热材料的制备、结构及应用研究进展

钠离子电池沥青基碳负极材料制备技术研究进展

基于金纳米颗粒修饰二氧化硅纳米花的生物传感器构建及应用

WC/TiO2纳米复合材料晶相形成机理及电催化性能

Crystal phase formation mechanism and electrocatalytical properties of WC/TiO2 nanocomposites

DOI：10.11949/j.issn.0438-1157.20160531

摘要

Abstract

关键词

Keywords

references

WC/TiO₂纳米复合材料晶相形成机理及电催化性能

Crystal phase formation mechanism and electrocatalytical properties of WC/TiO₂ nanocomposites