- 甲醇氧化制甲醛铁钼催化剂表面结构与活性
- Surface structure and activity of iron molybdate catalyst for methanol oxidation to formaldehyde
- 化工学报 2016年第9期页码：3678-3683
- 作者机构：
  
  1. 清华大学化学工程系,北京,100084
  2. 天津理工大学化学化工学院,天津,300384
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20160132
  中图分类号： 643
- 网络首发：2016-09-05，
  
  纸质出版：2016-09-05
- 稿件说明：
移动端阅览
张帅, 张一科, 呼日勒朝克图, 等. 甲醇氧化制甲醛铁钼催化剂表面结构与活性[J]. 化工学报, 2016,(9):3678-3683.

ZHANG Shuai, ZHANG Yike, HU Rlckt, et al. Surface structure and activity of iron molybdate catalyst for methanol oxidation to formaldehyde[J]. CIESC Journal, 2016, (9): 3678-3683.
张帅, 张一科, 呼日勒朝克图, 等. 甲醇氧化制甲醛铁钼催化剂表面结构与活性[J]. 化工学报, 2016,(9):3678-3683. DOI： 10.11949/j.issn.0438-1157.20160132.

ZHANG Shuai, ZHANG Yike, HU Rlckt, et al. Surface structure and activity of iron molybdate catalyst for methanol oxidation to formaldehyde[J]. CIESC Journal, 2016, (9): 3678-3683. DOI： 10.11949/j.issn.0438-1157.20160132.

摘要

利用共沉淀法在不同搅拌速度下制备了相同Mo/Fe原子比的甲醇氧化制甲醛催化剂，采用SEM、XRD和拉曼光谱等对催化剂进行表征，在固定床微反上评价催化剂活性和选择性。结果表明，搅拌速度增大，催化剂比表面积增大，催化活性增强，甲醛收率由600 r·min-1时的73.8%增加到10000 r·min-1时的95.7%（280℃）。此外，催化剂由片状的MoO3和颗粒状的Fe2（MoO4）3两部分组成，游离的片状MoO3无明显催化活性，只有与Fe2（MoO4）3结合时才具有催化活性。

Abstract

Iron-molybdenum catalysts with the same atomic ratio of Mo/Fe for methanol oxidation to formaldehyde were prepared by co-precipitation method under varied rates of stirring. The catalysts were characterized by SEM

XRD and Raman spectrum and the catalytic activity and selectivity evaluated in a fixed-bed reactor.It showed that with an increase of stirring speed

the specific surface area of the catalysts increases and the catalytic activity enhances. The yield of formaldehyde increases from 73.8% at 600 r·min-1 to 95.7% (T=280℃) at 10000 r·min-1. The catalyst consists of plate-like MoO3 and amorphous sponge-like Fe2(MoO4)3. In addition

the catalyst consists of sheet-shaped MoO3 and particle-shaped Fe2(MoO4)3

of which the former had barely no activity

and only the combination of the former and the latter (Fe2(MoO4)3) does show the catalytic activity.

关键词

Keywords

references

浏览量

383

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

微通道连续沉淀法制备球形BaTiO3颗粒及其在医学检测干片上的应用

钠基干法脱硫灰协同飞灰脱钙工艺路径研究

基于预辐射接枝法的DMAPS改性PVDF超亲水膜的制备及其油/水乳液分离性能

多孔纤维的制备及应用研究进展

干水材料抛撒药剂的性能及应用