Co-Fe<sub>2</sub>O<sub>3</sub>[104]铁基载氧体优化体系作用下褐煤化学链燃烧特性

覃吴; 侯翠翠; 张俊姣; 肖显斌; 程伟良; 董长青; 杨勇平

doi:10.11949/j.issn.0438-1157.20151309

您当前的位置：

首页 >

文章列表页 >

Co-Fe₂O₃[104]铁基载氧体优化体系作用下褐煤化学链燃烧特性

能源和环境工程 | 更新时间：2025-12-10

- Co-Fe₂O₃[104]铁基载氧体优化体系作用下褐煤化学链燃烧特性
- Chemical looping combustion characteristics of lignite using Co-Fe₂O₃[104]/Al₂O₃ oxygen carrier
- 化工学报 2016年第4期页码：1459-1466
- 作者机构：
  
  华北电力大学生物质发电成套设备国家工程实验室,北京,102206
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20151309
  中图分类号： K16
- 网络首发：2016-04-05，
  
  纸质出版：2016-04-05
- 稿件说明：
移动端阅览
覃吴, 侯翠翠, 张俊姣, 等. Co-Fe₂O₃[104]铁基载氧体优化体系作用下褐煤化学链燃烧特性[J]. 化工学报, 2016,(4):1459-1466. DOI: 10.11949/j.issn.0438-1157.20151309.

QIN Wu, HOU Cuicui, ZHANG Junjiao, et al. Chemical looping combustion characteristics of lignite using Co-Fe₂O₃[104]/Al₂O₃ oxygen carrier[J]. CIESC Journal, 2016, (4): 1459-1466. DOI: 10.11949/j.issn.0438-1157.20151309.
覃吴, 侯翠翠, 张俊姣, 等. Co-Fe₂O₃[104]铁基载氧体优化体系作用下褐煤化学链燃烧特性[J]. 化工学报, 2016,(4):1459-1466. DOI: 10.11949/j.issn.0438-1157.20151309. DOI：

QIN Wu, HOU Cuicui, ZHANG Junjiao, et al. Chemical looping combustion characteristics of lignite using Co-Fe₂O₃[104]/Al₂O₃ oxygen carrier[J]. CIESC Journal, 2016, (4): 1459-1466. DOI: 10.11949/j.issn.0438-1157.20151309. DOI：

摘要

前期研究发现高弥勒指数晶面载氧体Fe2O3[104]具有高的化学链燃烧反应特性

且Co对煤及其热解中间产物具有催化气化和催化转化作用。通过正交实验优化制备Co-Fe2O3[104]/Al2O3载氧体体系结构

开展Co-Fe2O3[104]/Al2O3与褐煤的化学链燃烧

揭示载氧体与褐煤发生化学链燃烧的特性。结果表明:形貌控制制备的高弥勒指数晶面铁基载氧体Co-Fe2O3[104]/Al2O3(质量分数10%)促进了褐煤化学链燃烧过程中氧的迁移速率以及载氧体的还原程度

进而显著提高了载氧体与褐煤化学链燃烧的反应速率及反应效率。进一步通过CO多循环化学链燃烧反应、XRD和TEM表征了Co-Fe2O3[104]/Al2O3(10%)的可再生性及反应稳定性。

Abstract

Previous works suggested that the iron-based oxygen carrier Fe2O3 with high- index facets [104] showed high activity during chemical looping combustion (CLC). It was also found that Co could be an efficient catalyst for catalytic gasification and conversion of coal. So

an optimized oxygen carrier system Co-Fe2O3[104]/Al2O3 was prepared through orthogonal experiments

and using it as oxygen carrier CLC of lignite was conducted to reveal its features. The results showed that Co-Fe2O3[104]/Al2O3(10%

mass fraction) prepared by morphology control can accelerate oxygen transport and its reduction

leading to an obvious increase of rate and efficiency for the reaction between the oxygen carrier and lignite. Furthermore

multi-cycle CLC of CO

XRD and TEM had been used to characterize the regeneration ability and the stability of optimized Co-Fe2O3[104]/Al2O3(10%).

关键词

Keywords

references

浏览量

301

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

镍基载氧体化学链燃烧过程中宁夏QH和YCW煤分子结构演化特征及对比分析

Li3VO4修饰富镍LiNi0.8Co0.1Mn0.1O2正极材料的电化学性能

单分散Co3O4@SiO2核壳催化剂的制备及N2O催化分解性能

具有自载体功能的CoFeAlO4载氧体化学链燃烧反应特性

共沉淀法制备LiNi1-x-yCoxMnyO2正极材料工艺条件探究

Co-Fe2O3[104]铁基载氧体优化体系作用下褐煤化学链燃烧特性

Chemical looping combustion characteristics of lignite using Co-Fe2O3[104]/Al2O3 oxygen carrier

DOI：10.11949/j.issn.0438-1157.20151309

摘要

Abstract

关键词

Keywords

references

Co-Fe₂O₃[104]铁基载氧体优化体系作用下褐煤化学链燃烧特性

Chemical looping combustion characteristics of lignite using Co-Fe₂O₃[104]/Al₂O₃ oxygen carrier