密闭空间低浓度CO<sub>2</sub>固态胺吸附剂长寿命评价

余青霓; 斯文婷; 杨彬; 朱京科; 雷乐成

doi:10.11949/j.issn.0438-1157.20150870

您当前的位置：

首页 >

文章列表页 >

密闭空间低浓度CO₂固态胺吸附剂长寿命评价

能源和环境工程 | 更新时间：2025-12-10

- 密闭空间低浓度CO₂固态胺吸附剂长寿命评价
- An assessment of life-cycles on solid amine for adsorbing low-concentration CO₂ in confined spaces
- 化工学报 2015年第9期页码：3692-3697
- 作者机构：
  
  1. 浙江大学化学工程与生物工程学院,浙江,杭州,310029
  2. 中国航天员科研训练中心,北京,100094
- 作者简介：
- 基金信息：
- DOI：10.11949/j.issn.0438-1157.20150870
  中图分类号： 552.3
- 网络首发：2015-09-05，
  
  纸质出版：2015-09-05
- 稿件说明：
移动端阅览
余青霓, 斯文婷, 杨彬, 等. 密闭空间低浓度CO₂固态胺吸附剂长寿命评价[J]. 化工学报, 2015,(9):3692-3697. DOI: 10.11949/j.issn.0438-1157.20150870.

YU Qingni, SI Wenting, YANG Bin, et al. An assessment of life-cycles on solid amine for adsorbing low-concentration CO₂ in confined spaces[J]. CIESC Journal, 2015, (9): 3692-3697. DOI: 10.11949/j.issn.0438-1157.20150870.
余青霓, 斯文婷, 杨彬, 等. 密闭空间低浓度CO₂固态胺吸附剂长寿命评价[J]. 化工学报, 2015,(9):3692-3697. DOI: 10.11949/j.issn.0438-1157.20150870. DOI：

YU Qingni, SI Wenting, YANG Bin, et al. An assessment of life-cycles on solid amine for adsorbing low-concentration CO₂ in confined spaces[J]. CIESC Journal, 2015, (9): 3692-3697. DOI: 10.11949/j.issn.0438-1157.20150870. DOI：

摘要

在密闭空间实际工况下

通过两组平行对照试验

考察了长时间吸脱附循环对固态胺材料CO2吸附性能的影响

对材料进行长寿命试验

并验证一年内固态胺材料性能的稳定性。结果表明

两组试验分别经过2128轮和2267轮吸脱附循环后

固态胺材料仍表现出良好的吸脱附稳定性。在长寿命试验条件下

两组吸附剂的CO2的吸附量维持在约28 mg·g-1

有机胺含量未见流失

活性胺含量比初始材料有所提高并不再降低

材料机械强度未受到影响。结果证明

高分子树脂基固态胺材料不仅能在室温条件下高效吸附CO2

且能在温和条件下实现CO2的解吸

在减少能耗的同时还有利于材料使用寿命的延长

适宜作为太空密闭空间中去除低浓度CO2的吸附材料

为航天员的生命保障提供技术支撑。

Abstract

To meet the requirement of a life support system

it is essential to develop an adsorbent with high stability and efficiency for removing low-concentration CO2 in confined spaces

such as spacecraft

space laboratory and submarine. Solid amine adsorbent was prepared by impregnating a polymer substrate with tetraethylenepentamine (TEPA)

and its performance and stability in adsorption/desorption cycles under actual working condition for the removal of CO2 in confined spaces were examined. Test of long period life (about one year) was carried out to verify its stability. The results showed that the adsorption performance remained stable after 2128 and 2267 cycles. Under the condition of the life tests

CO2 adsorption capacities were maintained at ～28 mg·g-1. Moreover

no significant loss of organic amine was found according to thermal analysis and CO2 titration

and the high mechanical strength was still kept. It demonstrated that high adsorption efficiency of CO2 on the solid amine adsorbent at room temperature (20℃) was achieved and the CO2 desorption process can be conducted at the mild conditions (30℃)

which is not only beneficial for reduction of energy consumption but also extend the service life. Therefore

the solid amine adsorbent

TEPA supported onto polymer substrate

could effectively be alternative for removal of CO2 in confined spaces.

关键词

Keywords

references

浏览量

1437

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

掺杂Ce、Zr对CO2钙基吸附剂循环特性的影响

高稳定铪金属-有机骨架材料的合成及二氧化碳捕获性能

铪金属-有机骨架材料的孔尺寸调控及其吸附性能

混合胺改性SBA-15的二氧化碳吸附特性

煤/生物质流态化富氧燃烧的CO2富集特性

密闭空间低浓度CO2固态胺吸附剂长寿命评价

An assessment of life-cycles on solid amine for adsorbing low-concentration CO2 in confined spaces

DOI：10.11949/j.issn.0438-1157.20150870

摘要

Abstract

关键词

Keywords

references

密闭空间低浓度CO₂固态胺吸附剂长寿命评价

An assessment of life-cycles on solid amine for adsorbing low-concentration CO₂ in confined spaces